Enhanced Antimicrobial Activity of AgCu Nanoparticles: The Role of Particle Size and Alloy Composition

Yuping Le,Fang Zhou,Longlai Yang,Yan Zhu,Dequan Yang

DOI: https://doi.org/10.3390/molecules29133027

IF: 4.6

2024-06-27

Molecules

Abstract:AgCu bimetallic· nanoparticles (NPs) represent a novel class of inorganic, broad-spectrum antimicrobial agents that offer enhanced antimicrobial effectiveness and reduced cytotoxicity compared to conventional Ag NP antibacterial materials. This study examines the antimicrobial performance and structural characteristics of AgCu nanoparticles (NPs) synthesized via two distinct chemical reduction processes using PVP-PVA as stabilizers. Despite identical chemical elements and sphere-like shapes in both synthesis methods, the resulting AgCu nanoparticles exhibited significant differences in size and antimicrobial properties. Notably, AgCu NPs with smaller average particle sizes demonstrated weaker antimicrobial activity, as assessed by the minimum inhibitory concentration (MIC) measurement, contrary to conventional expectations. However, larger average particle-sized AgCu NPs showed superior antimicrobial effectiveness. High-resolution transmission electron microscopy analysis revealed that nearly all larger particle-sized nanoparticles were AgCu nanoalloys. In contrast, the smaller particle-sized samples consisted of both AgCu alloys and monometallic Ag and Cu NPs. The fraction of Ag ions (relative to the total silver amount) in the larger AgCu NPs was found to be around 9%, compared to only 5% in that of the smaller AgCu NPs. This indicates that the AgCu alloy content significantly contributes to enhanced antibacterial efficacy, as a higher AgCu content results in the increased release of Ag ions. These findings suggest that the enhanced antimicrobial efficacy of AgCu NPs is primarily attributed to their chemical composition and phase structures, rather than the size of the nanoparticles.

chemistry, multidisciplinary,biochemistry & molecular biology

What problem does this paper attempt to address?

The problem this paper attempts to address is: How do the antibacterial properties of silver-copper nanoparticles (AgCu NPs) get affected by particle size and alloy composition? Specifically, the researchers synthesized AgCu nanoparticles using two different chemical reduction methods and investigated the antibacterial effects of these particles at different sizes and structures. The main aim of the study is to reveal the relationship between particle size, alloy composition, and antibacterial properties, thereby providing a theoretical basis for developing more effective antibacterial materials.

### Main Issues:
1. **Effect of particle size on the antibacterial properties of AgCu nanoparticles**: It is generally believed that smaller nanoparticles have better antibacterial effects, but this study found that larger AgCu nanoparticles exhibited stronger antibacterial activity.
2. **Effect of alloy composition on the antibacterial properties of AgCu nanoparticles**: The study found that nanoparticles with a higher AgCu alloy content released more silver ions, thereby enhancing the antibacterial effect.
3. **Effect of particle structure on the antibacterial properties of AgCu nanoparticles**: Through high-resolution transmission electron microscopy (HR-TEM) analysis, researchers found that larger AgCu nanoparticles were mainly composed of AgCu alloy, while smaller particles contained single-metal Ag and Cu nanoparticles, which further affected the antibacterial properties.

### Research Background:
- Silver nanoparticles (Ag NPs) and their alloys have attracted widespread attention due to their excellent antibacterial properties, especially in fields such as medical, medical devices, and consumer products.
- Antibacterial properties are influenced by various factors, including particle size, shape, surface physicochemical properties, and surrounding chemical environment.
- The traditional view is that smaller silver nanoparticles have higher antibacterial activity because they have a larger surface area-to-volume ratio and can more easily penetrate bacterial cell walls.
- However, producing extremely small silver nanoparticles and their alloys poses challenges in manufacturing and stability, so a balance needs to be found to ensure good antibacterial performance and feasibility in manufacturing and storage.

### Research Methods:
- **Synthesis Method**: AgCu nanoparticles were synthesized using two different chemical reduction methods, with PVP-PVA used as a stabilizer.
- **Characterization Method**: Transmission electron microscopy (TEM) and high-resolution transmission electron microscopy (HR-TEM) were used to analyze the morphology and structure of the particles.
- **Antibacterial Performance Testing**: Antibacterial performance was evaluated by measuring the minimum inhibitory concentration (MIC) and minimum bactericidal concentration (MBC).
- **Silver Ion Release Measurement**: The release amount of silver ions was measured by inductively coupled plasma mass spectrometry (ICP-MS).

### Research Results:
- **Particle Size**: The average particle size of the AgCu-1# sample was about 4 nm, while the average particle size of the AgCu-2# sample was about 30 nm.
- **Antibacterial Performance**: Despite the larger particle size of the AgCu-2# sample, its antibacterial performance was better than that of the AgCu-1# sample.
- **Silver Ion Release**: The release amount of silver ions in the AgCu-2# sample was higher than that in the AgCu-1# sample, indicating that nanoparticles with a higher AgCu alloy content have better antibacterial effects.

### Conclusion:
- The antibacterial properties of AgCu nanoparticles are influenced not only by particle size but also by particle structure and alloy composition.
- Larger AgCu nanoparticles, due to containing more AgCu alloy, can release more silver ions, thereby exhibiting stronger antibacterial activity.
- This finding provides new insights for developing more effective antibacterial materials, especially in optimizing particle structure and composition.