Neodymium Dysprosium Modified Starch-coated Magnetic Fluid Preparation of Ferrite

Zhou Yu

Abstract:In this paper,in order to obtain the ferrite magnetic fluids of higher saturation magnetic intensity with simple technology,nanometer magnerite(Fe3O4) particles ware prepared by chemical co-precipitation.And to a certain proportion of Dysprosium Neodymium ferrite magnetic fluids on the modification,we selected starch preparation for the relief of water-based coating of rare earth iron oxide magnetic fluid composites.We also investigated the amount of Nd-Dy,the amount of coating agent,reaction temperature,coating temperature on the performance of the products and the effects of particle size,and its preliminary characterization was also performed.Through experiment,we summed up,under n(Fe):[n(Nd3+)+n(Dy3+)]=30:1 and n(Fe3+):n(Fe2+)=1.70~1.75,the ratio for use of dysprosium and neodymium is n(Dy3+): n(Nd3+)=4:1,25%NH3·H2O(A.R.) as precipitating agent and pH value conditioner;the reacting system temperature was controlled in 35℃,and the pH value was adjusted to 9 ~ 11;the best dosage of starch as the relief is 0.0050g each 60mL magnetic fluids,the temperature of surfactant was controlled in 50 ℃ and the pH value was adjusted to 2~3.In such system under the conditions of a water-based rare-earth compound Nd Dy Fe Magnetic,fluid magnetic oxygen was higher than ordinary water-based ferrite.

Materials Science