Infrared Femtosecond Fiber Laser Welding of Silica Glass with 304 Stainless Steel
Jinhui Yuan,Jingyu Huo,Boyuan Zhang,Lei Wang,Zhong Zheng,Jiaming Li,Liang Guo,Aiping Luo,Qingmao Zhang
DOI: https://doi.org/10.3788/cjl231406
2024-01-01
Abstract:Objective Glass?metal connections can expand the applications of glass in many industrial fields, and glass connectors have been widely used in semiconductor devices, automotive manufacturing, and other industries. Joints fabricated by the traditional bonding method have a low working temperature and can easily produce volatile gases, which limit their application range. However, laser welding has the advantages of high energy density, noncontact, small heat-affected area, and high welding accuracy, which can realize high-quality glass?metal connections. In recent years, the technology of ultrashort pulse laser welding of dissimilar materials has received increasing research attention. However, temperature field simulations of femtosecond laser welding of dissimilar materials have rarely been reported, and the effects of laser single-pulse energy on weld quality must be further studied. In this study, the effects of femtosecond pulse laser welding energy on the weld morphology, welding strength, and welding mechanism were studied, and the temperature field in the welding process was analyzed using a finite element model. Methods In this study, a two-dimensional axisymmetric geometric model was established, and a Gaussian body heat source was applied at the middle interface of the model. A finite element simulation of the temperature field of the femtosecond pulse laser welding of silica glass and 304 stainless steel was conducted to verify the feasibility of the welding parameters. The femtosecond pulse laser wavelength, pulse width, repetition rate, and laser single-pulse energy were 1030 nm, 300 fs, 500 kHz, and 4.2?7.8 mu J, respectively. In the experiment, the treated silica glass was tightly bonded with 304 stainless steel to enable the sample to reach the optical contact state and was then placed on the laser welding platform. Following adjustments to the focus position through the displacement platform in the z direction, the laser was focused on the interface between the silica glass and 304 stainless steel for welding. After the welded sample was subjected to a shear test, the weld morphology and elemental distribution were analyzed. Results and Discussions According to the calculation, at the lower single-pulse energy of 4.2 mu J, the maximum temperature of the interface between the silica glass and 304 stainless steel is 4101 K (Fig.4), which is higher than the softening temperature of silica glass and the melting point of 304 stainless steel at 1857 and 1727 K, respectively. With an increase in the laser single-pulse energy, the time required for the electronic and lattice systems to reach thermal equilibrium increases. Under confocal laser scanning microscopy (CLSM) to observe the welding area through silica glass, at >= 6.8 mu J, the thermal stress is too large, exceeding the damage threshold of silica glass, and microcracks form at the edge of the weld [Fig.5(a)]. After the samples were separated, the weld surface and sections were examined using scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). No obvious melting traces are observed on the weld surface, and only the presence of many dot structures is observed. The dot structure on the 304 stainless steel side is composed of particles extending from the weld [Fig.6(b)], whereas that on the silica glass side is composed of holes [Fig.6(d)]. The interface between the silica glass and 304 stainless steel is clear, and no mechanical interlocking structure is formed [Fig.8(a)]. On the 304 stainless steel side, Si deposition can be observed in each weld as compared with the substrate [Fig.8(d)], and the distribution of Si in most welds is symmetrical along the weld center [Fig.8(f)], indicating that the diffusion of Si is related to the distribution of laser energy. Using XRD to detect the phase of the sample, we find that the austenite content of the 304 stainless steel decreases and the martensite content increases under the action of the laser [Fig.9(a)]. However, the welded silica glass exhibits no biological phase change [Fig.9(b)]. Raman spectrometry was used to detect the blank and welding areas of the silica glass, and the welds show characteristic peaks of silica glass. This indicates that following the shear test, reduced weld residue is present on the glass side, which is otherwise difficult to detect [Fig.9(c)]. Conclusions In this study, a finite element simulation of the temperature field during the welding process determines that heat accumulates during the femtosecond laser welding process. According to calculations, the highest welding temperature is higher than the softening temperature of silica glass and the melting point of 304 stainless steel at 1857 and 1727 K, respectively, indicating the feasibility of welding. With the optimal parameters, the shear strength reaches 13 MPa. Combining silica glass with 304 stainless steel proves difficult under single-pulse energy of less than 4.2 mu J. Between 4.2 and 5.6 mu J, no significant change is apparent in the welding area. When single-pulse energy reaches or over 6.8 mu J, microcracks appear in the weld seam. This study also utilized testing and analytical methods such as SEM, XRD, and Raman spectroscopy, to investigate the mechanism of femtosecond laser welding of silica glass and 304 stainless steel. SEM, EDS, and other testing methods indicate that Fe and Cr may undergo redox reactions with SiO2 at the interface, forming Fe2O3 and Cr2O3.