Bimetallic doping-derived heterostructures in NiCo-WSe 2 to promote hydrogen evolution reaction
Feng-bo Guo,Xin-ya Zhao,Hai-yu Lei,Yan Xu,Kan-kan Liu,Li-xin Zhang,Jie-min Xue,Hua-ran Sun
DOI: https://doi.org/10.1016/j.jallcom.2022.166538
IF: 6.2
2022-08-06
Journal of Alloys and Compounds
Abstract:The application of transition metal dichalcogenides (TMDs) in hydrogen evolution reaction (HER) is limited due to fewer edge active sites and poor conductivity. Appropriate transition metal dopants on TMDs are an important strategy. Herein, the Fe, Cu, Mo, Ni, and Co doped WSe 2 have been synthesized. Compared with pristine WSe 2 , the results show that the overpotential of WSe 2 was significantly reduced after doping, and the order of activity was ranked as follows: Co-WSe 2 > Ni-WSe 2 > Mo-WSe 2 > Fe-WSe 2 > Cu-WSe 2 . Among them, Co-WSe 2 showed a smaller overpotential and charge transfer resistance, and Ni-WSe 2 exhibited a larger electrochemically active surface area and a smaller Tafel slope. Further, NiCo-WSe 2 was also prepared, which has an overpotential of 205 mV at 10 mA cm −2 and a tafel slope of 118.6 mV dec −1 , respectively. Crystal structure analysis shows that CoSe 2 is agglomerated in Co-WSe 2 , but it is uniformly distributed on the surface of NiCo-WSe 2 because the competitive substitution effect between Ni and Co slows down the growth rate of CoSe 2 , and thus providing more efficient interfacial active site. In addition, the higher electronegativity of Ni and Co reduces the electron density around W and Se, which changes the electronic structure of WSe 2 and accelerates the mass transfer efficiency between charges, thereby promoting the HER performance of NiCo-WSe 2 . This work provides a technological pathway for the development of inexpensive and commercializable HER electrocatalysts.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering