Soft magnetic properties regulation of FeSiBC amorphous powders/CIP magnetic powder core with single and double-layer core-shell structure
Pu Wang,Zhengqu Zhu,Jiaqi Liu,Huan Zhao,Jing Pang,Jiaquan Zhang
DOI: https://doi.org/10.1016/j.jmmm.2023.170809
IF: 3.097
2023-05-08
Journal of Magnetism and Magnetic Materials
Abstract:In this study, an equal proportion of carbonyl iron powder (CIP) was added to the FeSiBC amorphous powders, then three kinds of composite powders, namely (epoxy resin) with a single-layer core-shell structure, 2 (silica powder)@EP and (silicone resin)@EP with a double-layer core-shell structure, were synthesized and prepared into corresponding SMPCs (soft magnetic powder cores). The results show that the FeSiBC amorphous powders exhibit good sphericity, a high saturation magnetization (153.534 emu∙g -1 ), and a wide undercooled liquid region (△ T =51 K). When mixed with CIP, its saturation magnetization increased from 153.534 emu∙g -1 to 189.875 emu∙g -1 , which is an ideal raw material for preparing SMPCs. The three SMPCs after insulation coating treatment have high permeability (29.3∼34.2), high DC bias performance (76.26∼84.11, 100 Oe), and low core loss (762.66∼902.69 mW·cm -3 , 200 Gs, 1000 kHz), and excellent overall soft magnetic performance. Finally, the loss separation analysis of the magnetic core loss of SMPCs shows that the loss of @EP soft magnetic powder cores with a double-layer organic core-shell structure is only 762.66 mW·cm -3 at 200 Gs and 1 MHz, which is much lower than that of SMPCs with a single-layer core-shell structure (902.69 mW·cm -3 , 200 Gs, 1000 kHz). At the same time, the permeability of SMPCs (31.0) is relatively high, and the comprehensive performance is good in the high-frequency range.
materials science, multidisciplinary,physics, condensed matter