MnOx Embedded in Silicon Nanowire Arrays for High-Performance Supercapacitors

Pengwei Liu,Manlin Wei,Xiaojuan Shen

DOI: https://doi.org/10.1007/s10904-024-03415-7

IF: 3.518

2024-09-26

Journal of Inorganic and Organometallic Polymers and Materials

Abstract:Due to the good integration with the current silicon-based electronic devices, silicon-based supercapacitor have been considered as one of the promising energy storage devices. However, their practical application is largely hindered by complex and costly manufacturing processes. In this study, a novel NiSi@MnO x electrode was fabricated with a simple and cost-effective method, where Ni nanoparticles and MnO x nanoparticles were sequentially electrodeposited on the silicon nanowire arrays (SiNWs). Ni particles served as the protective layer on the silicon surface as well as the current collector of the composite, and MnO x functioned as the electrochemical material of the electrode. As the deposition time of MnO x increased, the structure of NiSi@MnO x changed from core–shell to embedded. The electrochemical results demonstrated that when MnO x was embedded in Silicon nanowires, the NiSi@MnO x electrode achieved an excellent area capacitance of 328.6 mF/cm 2 at 1 mA/cm 2 , which also displayed an impressive capacitance retention of 79.05% after 7000 cycles. Additionally, an all-solid-state asymmetric SC (ASC) of NiSi@MnO x //Fe 2 O 3 /N-rGO was fabricated by using NiSi@MnO x as positive electrode, Fe 2 O 3 /N-rGO loaded on NF as negative electrode. The ASC exhibited a remarkable energy density of 0.021 mWh/cm 2 at the power density of 0.7998 mW/cm 2 , surpassing the majority of reported values for silicon-based/MnO x -based supercapacitors. This study provides a simple, time-effective, and low-cost method to prepare high-performance 3D silicon-based electrodes.

polymer science