Sol-gel synthesized double perovskite Na(1-)Gd(0.95+/3)MgWO6: 5% Eu3+ (0 ≤ x ≤ 0.5) phosphors with incommensurately modulated structure: Microstructures and luminescence properties

Zhengdong Wu,Shenghao Ai,Huan Chen,Ting Zhou,Mengjiao Liu,Yan Zhao,Xin Lai,Jian Bi,Daojiang Gao

DOI: https://doi.org/10.1016/j.optlastec.2022.107947

2022-06-01

Abstract:A series of Eu3+-activated double perovskite Na(1- x )Gd(0.95+ x /3)MgWO6: 5% Eu3+ (0 ≤ x ≤ 0.5) phosphors were successfully synthesized via sol–gel route, the effects of the variation of x on the microstructure and luminescent properties of the synthesized phosphors were studied in detail. It is found that all of the obtained phosphors are irregular polyhedral crystals with the average grain size of ∼0.5–1 μm, exhibiting a monoclinic double perovskite structure. All of the Na(1- x )Gd(0.95+ x /3)MgWO6: 5% Eu3+ (0 ≤ x ≤ 0.5) phosphors can be efficiently excited by blue light (464 nm) and near ultraviolet light (395 nm), showing promising application in white light-emitting diodes. Interestingly, the charge transfer band of the Na(1- x )Gd(0.95+ x /3)MgWO6: 5% Eu3+ (0 < x ≤ 0.5) phosphors has slight shift compared with the as-synthesized NaGd0.95MgWO6: 5% Eu3+ phosphor. Upon excitation of 464 nm and 395 nm lights, these phosphors can exhibit the strongest red emission at 615 nm, and the red emission intensity gradually increases with ascending x and then markedly decreases, showing the largest at x = 0.2. Especially, the obtained Na0.8Gd(0.95+1/15)MgWO6: 5% Eu3+ phosphor possesses the best luminescence properties, including the highest emission intensity at room temperature, optimal thermal stability and the better photoelectric parameters for the packaged WLED.

optics,physics, applied