Abstract:To reduce carbon emissions associated with substantial concrete usage in construction and achieve the objectives of green and low-carbon construction, this study innovatively develops a low-carbon binary material by adding limestone powder (LP) and silica fume (SF) into the conventional cement-based material, enhancing the comprehensive utility value of LP. The experimental results show that the addition of 15% LP and 5% SF increases the yield stress of the mortar yet substantially reduces the plastic viscosity to 2.84 Nmm·min, representing a 44.5% decrease compared to pure cement slurry. This reduction is conducive to long-distance pumping of the cement-based material. Moreover, the addition of 5% SF compensates for the 18.8% (mid-stage, 28-d) and 15.8% (late-stage, 90-d) strength loss in mortar caused by LP while simultaneously improving the strength of the co-mixed system by 10.4% (mid-stage) and 10.8% (late-stage). In the early-stage measurements of the LP-SF binary cement-based materials, it is observed that while SF slightly increases the hydration heat release, LP suppresses the early hydration heat release. Therefore, the total heat release observed in the 15% LP and 5% SF group after 72 h is only 254 J/g, demonstrating favorable temperature control and crack prevention effects. In addition, X-ray diffraction (XRD) and thermogravimetric/differential thermogravimetric (TG/DTG) phase analysis reveal a notable increase of 53.56% in CH consumption. Besides, the weight loss on ignition of C-S-H crystals increases, indicating that the secondary hydration of LP and the pozzolanic reaction of SF promote the production of C-S-H in the system. Combined with the late-stage strength and water absorption characteristics, it is concluded that the system exhibits good mechanical properties and compactness. This study presents a use of mixed proportion that enables excellent mechanical properties, good pumping performance, and low hydration heat. Moreover, the analysis indicates that the carbon emission of each cubic meter of the as-developed mortar is reduced by approximately 16.7–23.9%, promoting the efficient and clean utilization of LP and SF.

Effects of Lime Powder on the Properties of Portland Cement–Sulphoaluminate Cement Composite System at Low Temperature

Microstructure Refinement of Calcium-Sulfate-aluminate and Portland Cement (CSA-PC) Hybrids with Accelerated CO2 Curing (ACC)

Effect of the fineness of limestone powder on the properties of calcium sulfoaluminate cement

Study on the Frost Resistance of Composite Limestone Powder Concrete against Coupling Effects of Sulfate Freeze–Thaw

Properties of Concrete with High-Volume Limestone Powder under Low Temperature Conditions

Early Age Performance of OPC-GGBFS-Concretes Containing Belite-CSA Cement Cured at Sub-Zero Temperatures

Optimizing anti-freezing agent on the properties of Portland cement-calcium sulphoaluminate cement system based on Taguchi-GRA method

Effect of n-C-S-H on Hydration and Reinforcement of Mineral Powder-Cement System at Low Temperatures

Effect of High Content Limestone Powder on Microstructure and Mechanical Properties of Cement-based Materials

Effects of Tuff Powder on the Hydration Properties of Cement-Based Materials under High Temperature

Examining the early-stage performance and mechanical performance of limestone powder-silica fume binary cement-based materials

A green binder for cold weather applications: enhancing mechanical performance of alkali-activated slag through modulus, alkali dosage, and Portland cement substitution

Effect of polycarboxylate superplasticizer and calcium nitrite on the fluidity and early strength of belite sulfoaluminate cement

Early Hydration Heat of Calcium Sulfoaluminate Cement with Influences of Supplementary Cementitious Materials and Water to Binder Ratio

Long-term properties of concrete containing limestone powder

Effects of calcined phosphogypsum replacement on hydration and properties of calcium sulfoaluminate cement at different curing temperatures

How Competitive Hydration between C 3 A and C 3 S in the Fast Dissolution Stage Affects the Hydration of Low-Heat Portland Cement Blended Pastes

Influence of C–S–H seed and sodium sulfate on the hydration and strength of limestone calcined clay cement

Effect of calcium sulfoaluminate cement on the hydration process and water resistance of phosphogypsum slag cement

Effects of Accelerators and Retarders in Early Strength Development of Concrete Based on Low-Temperature-Cured Ordinary Portland and Calcium Sulfoaluminate Cement Blends

Effects of Lithium Slag on the Frost Resistance of Cement-Soil