Investigation on effects of tritium release behavior in Li4SiO4 pebbles

Qiang Qi,Mingzhong Zhao,Fei Sun,Yingchun Zhang,Shouxi Gu,Baolong Ji,Hai-Shan Zhou,Yasuhisa Oya,Songlin Liu,Guang-Nan Luo

DOI: https://doi.org/10.1016/j.nme.2021.101036

IF: 3.037

2021-09-01

Nuclear Materials and Energy

Abstract:For deuterium–tritium fusion reactor, the fuel of tritium is not available naturally. Tritium should be produced by the reaction of Li (n, ɑ) T. Li4SiO4 is one of promising candidates due to its high lithium density. In present work, effects of tritium release behavior from Li4SiO4 have been investigated and compared. The main release peak at lower temperature was attributed to tritium located on/near the grain surface and chemical adsorption on pore surface. The small peak at higher temperature was designated as tritium diffusion from grain including lattice and boundary. The tritium release behavior was simulated by diffusion model and surface reaction model. Tritium behavior is controlled by both diffusion and surface reaction for different stages. Based on the desorption theory, the kinetic parameters were obtained. The effects on tritium release behavior were studied. The porosity has significant effects on tritium release. Higher porosity has large specific surface providing more activation sites and fast channels for tritium release which results in lower temperature of tritium release. The main tritium release form was considered as tritium water. The release peak of deuterium moved towards lower temperature after adsorbing water vapor for 1800 h. It was demonstrated that adsorbing water was beneficial for tritium release due to isotope exchange. Compared the effects of porosity and water vapor, higher porosity has larger effects on tritium release in the present work. Based on the work, the tritium release is controlled by both diffusion and surface reaction at different stage and affected by comprehensive effects including porosity and adsorption water.

nuclear science & technology

What problem does this paper attempt to address?

### Problems the Paper Attempts to Solve

This paper aims to investigate the factors influencing tritium release behavior in lithium orthosilicate (Li4SiO4) pebbles and to explore the tritium release mechanisms under different conditions. Specifically:

1. **Tritium Release Mechanism**:
- The study found that tritium release is mainly controlled by diffusion and surface reactions. In the initial stage, tritium release is primarily controlled by surface reactions; in the later stage, diffusion becomes the main controlling factor.
- By fitting experimental data, the diffusion model and surface reaction model were validated to explain the tritium release behavior.

2. **Effect of Porosity**:
- Samples with higher porosity have a larger specific surface area, providing more active sites, which is beneficial for lowering the tritium release temperature.
- Experimental results show that samples with 70% porosity release more tritium at lower temperatures compared to samples with 85% porosity.

3. **Effect of Adsorbed Water**:
- Adsorbed water facilitates tritium release, especially at lower temperatures. Through deuterium release simulation experiments, it was found that after being exposed to air for 1800 hours, the deuterium release peak shifted to a lower temperature, indicating that adsorbed water promotes isotope exchange reactions.

In summary, this paper explores the tritium release behavior and its influencing factors in lithium orthosilicate materials under different conditions through experimental and theoretical analysis, providing guidance for the design of future tritium breeding materials.