Confining Nano-GeP in Nitrogenous Hollow Carbon Fibers toward Flexible and High-Performance Lithium-Ion Batteries
Tianbiao Zeng,Dong Feng,Qi Liu,Ruoyu Zhou
DOI: https://doi.org/10.1021/acsami.1c07387
2021-07-07
Abstract:Although graphite has been used as anodes of lithium-ion batteries (LiBs) for 30 years, its unsatisfactory energy density makes it insufficient toward some new electronic products such as unmanned aerial vehicles. Herein, in situ synthesis of nano-GeP confined in nitrogen-doped carbon () fibers was designed and performed via coaxial electrospinning followed by a phosphating process. This way ensured the paper-like <i>x</i> electrode with high conductivity, high flexibility, and lightweight properties, which simultaneously solved the key scientific problems of difficulty in structural design and severe volume expansion of GeP. The inner diameter and wall thickness of the nanofibers can be effectively controlled by adjusting the size of electrospinning needles. It was suggested that the fibers not only effectively inhibited the growth of GeP, resulting in the synthesis of nano-GeP with size less than 50 nm, but also alleviated the volume expansion/agglomeration and improved the diffusion kinetics of Li<sup>+</sup> in nano-GeP during cycling. The Li<sup>+</sup> diffusion coefficient can be improved by reducing the inner diameter and wall thickness of the fibers. As a model system, the paper-like electrode () with a fiber diameter of 280 nm and a wall thickness of 110 nm exhibited the best electrochemical performance. When applied as anodes in LiBs, it displayed a reversible capacity of 612 mAh g<sup>–1</sup> at the 600th cycle at 1 A g<sup>–1</sup>, while with a solid structure only delivered 239 mAh g<sup>–1</sup>. Furthermore, the also exhibited good long-term cycling stability at 5 A g<sup>–1</sup>, and the capacity displayed a slight difference of 221.2 and 209.0 mAh g<sup>–1</sup> in a voltage range of 0∼3 V and 0∼1.5 V, respectively. The well-defined synthetic approach combined with unique nanostructural design provided a meaningful reference for the rational design and development of next-generation flexible and high-performance LiB anodes.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c07387?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c07387</a>.Additional data analysis including digital photos (Figure S1), SEM images and C, Ge, P, and N elemental mapping images (Figure S2), TGA curves (Figure S3), and rate CV curves (Figure S4) of <i>x</i>. In addition to that, the XRD pattern, SEM image, CV curves, discharge/charge profiles, and cycling capacity of the LiNi<sub>0.8</sub>Co<sub>0.15</sub>Ai<sub>0.05</sub>O<sub>2</sub> cathode are supplied (Figure S5). Table S1 is the fitted data of each electronic components (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c07387/suppl_file/am1c07387_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology