Synthesis and performance of oleic acid-sodium dodecyl sulfate modified graphene/styrene-acrylic emulsion nanocomposites
Quan-tao LI,Hong-yu HU,Zheng-hui LI,Zu-shun XU,Jun-ting XU,Fa-rao ZHANG
DOI: https://doi.org/10.3969/j.issn.1001-5922.2019.02.004
2019-01-01
Abstract:Graphene (GE) was modified with oleic acid/sodium dodecyl sulfate (OA-SDS-GE), then the acrylic emulsion nanocomposites containing OA-SDS-GE were prepared via pre-emulsification and semi-continuous seed emulsion polymerization, by adjusting the proportions of monomers, such as styrene (St), methyl methacrylate (MMA), butyl acrylate (BA) and acrylic acid (AA), and using ammonium persulfate (APS) and sodium bicarbonate as the initiators, and the compounded emulsifiers. The structure, particle morphology and performance of the nanocomposites were studied, and the results showed that the emulsion with high solid content (42％) had better mechanical and dilution stability, the average particle size and polydispersity index (PDI) measured by PCS were 102.3 nm and 0.007, respectively. The TGA results revealed that the OA-SDS-GE/styrene-acrylic emulsion nanocomposites were thermally stable, and the 5％ and 10％thermal decomposition temperatures under N2 atmosphere were 351.0℃ and 376.2℃, respectively. The nanocomposites had a surface resistivity of 7.9×108 Ω after film formation and the film antistatic property was good.