Abstract:The meta- and para-catenated methylene-containing phthalonitrile oligomers were prepared from the reaction of an excess amount of 4,4 ′ -(4,4 ′ -isopropylidenediphenoxy) bis-(phthalic anhydride) (BPADA) with 4,4 ′ -Methylenedianiline (MDA) in a N, N-dimethylformamide/ toluene solvent mixture, followed by end-capping agent with 4-nitrophthalonitrile or 4-phenoxyaniline in a two-step, one-pot reaction. Differential scanning calorimetry (DSC) showed that both PN oligomers exhibited low softening points. The self-catalyzed curing reactivity of the PN oligomers was confirmed by the isothermal rheological measurements. Fourier transform infrared spectroscopy (FTIR) and ultraviolet and visible spectrophotometry (UV–Vis) data of the pre-curing resins were employed to investigate the chemical structure of the pre-cured resins, suggesting that oligomers generated crosslinking sites, including triazine, isoindoline, and phthalocyanine. The results further confirmed the self-catalyzed curing reactivity of the oligomers. Thermal properties were investigated by dynamic mechanical analysis (DMA) and thermal gravimetric analysis (TGA), demonstrating good thermal properties of the cured resins. The glass transition temperatures (T g s) of PIPN-1-325, PIPN-1-350, PIPN-1-375 were in the range of 285–345°C, the 5% weight loss temperature (T 5% ) was observed at 482°C. The PIPN-2-325, PIPN-2-350, PIPN-2-375 showed T g s ranging from 293 to 370°C, and T 5% of the resins were in the range of 481–501°C. Then the isothermal rheological results of model compound and PN oligomers implied that the curing process of PN oligomers was closely related to the methylene-cyano radical thermal synergistic polymerization (TSP) effect proposed in our previous research, and then a revised curing mechanism (radical TSP mechanism) was proposed.

A theoretical insight into the curing mechanism of phthalonitrile resins promoted by aromatic amines

Cure of Neat Resins and Properties of Composites for Interpenetrating Polymer Networks from the Novel Bismaleimide and Cyanate Containing Naphthalene

Synthesis, Curing, and Thermal Stability of Low-Temperature-Cured Benzoxazine Resins Based on Natural Renewable Resources

Interpenetrating polymer networks from the novel bismaleimide and cyanate containing naphthalene: Cure and thermal characteristics

Curing, Thermal Stability and Composite Properties for Blends of the Novel Bismaleimide and Cyanate Containing Naphthalene

Cure and thermal properties of cyanate ester resin containing naphthalene ring

Synthesis, characterization and self-promoted cure behaviors of a new phthalonitrile derivative 4-(4-(3, 5-diaminobenzoyl) phenoxy) phthalonitrile

Learning about novel amine-adduct curing agents for epoxy resins: Butyl-glycidylether-modified poly(propyleneimine) dendrimers

Synthesis and Curing of a Novel Combined Liquid Crystalline Epoxy

Cure Kinetics of an Epoxy Resin Containing Naphthyl/dicyclopentadiene Moieties and Bis‐phenoxy (3‐hydroxy) Phosphine Oxide System and Properties of Its Cured Polymer

Synthesis, Curing Kinetics, and Properties of a Novel Phthalazine‐Based Phthalonitrile Resin

Promoting effect of methyne/methylene moiety of bisphenol E/F on phthalonitrile resin curing: Expanding the structural design route of phthalonitrile resin

Synthesis of oligomeric phthalonitrile resins containing imide units and study of the methylene-cyano thermal synergistic polymerization effect

Curing kinetics and thermal properties of [2,2] paracyclophane/bisphthalonitrile-terminated imide resins

Polyaniline facilitated curing of phthalonitrile resin with enhanced processibility and mechanical property

Self-curing triphenol A-based phthalonitrile resin precursor acts as a flexibilizer and curing agent for phthalonitrile resin

Thermal curing mechanisms and cross-linking network structure of a novel silicon-containing arylacetylene resin with 2,7-diethynylnaphthalene unit

Effects of the Backbone's Structures on the Curing Behaviors and Properties of Phthalonitrile Containing Benzoxazine Rings

Synthesis, curing and thermal properties of the low melting point phthalonitrile resins containing glycidyl groups

The influence of phthalonitrile monomer containing oxazine ring on the properties of epoxy/amine system: Curing behavior and thermal stability

A new approach to enhance the performance of phthalonitrile: study of carborane curing agents with dual functions