Enhancement of physical and electrochemical properties of electrospun P(VdF-co-HFP) separators by incorporating magnesium borate for advanced lithium-ion batteries

Mohammed A.M.M. Al-SAMET,Simge Kara,Engin Burgaz

DOI: https://doi.org/10.1016/j.polymer.2024.127798

IF: 4.6

2024-11-08

Polymer

Abstract:In this study, fibrous membrane composites containing poly(vinylidene fluoride-co-hexafluoropropylene) P(VdF-co-HFP) copolymer and various amounts of magnesium borate Mg 2 B 2 O 5 were prepared via electrospinning method. The crystallization behavior, thermal stability, microstructure, porosity, liquid electrolyte uptake and electrochemical performance of electrospun membranes were investigated in detail. X-ray diffraction (XRD) and differential scanning calorimetry (DSC) show that, the crystallinity of P(VdF-co-HFP) tends to decrease with increasing amount of Mg 2 B 2 O 5 particles. The electrospun membrane containing P(VdF-co-HFP) and 2.5 wt.% of Mg 2 B 2 O 5 demonstrates stronger anti-shrinkage properties compared to those of commercial polypropylene (PP) or pure P(VdF-co-HFP) separators at 140 °C. The fibrous membrane consisting of 2.5 wt.% Mg 2 B 2 O 5 exhibits high electrolyte uptake (381%), low interfacial resistance and good porosity at room temperature (81%), even after heating at 140 °C the porosity becomes 78%. Moreover, Li||LiFePO 4 cell using P(VdF-co-HFP) separator with 2.5 wt.% of Mg 2 B 2 O 5 shows better discharge capacities of 167.5 and 146.8 mAh g −1 at 0.2 C and 5 C, respectively, compared to those of commercial PP separator which delivers only 158 and 127 mAh g -1 at 0.2 C and 5 C, respectively. [P(VdF-co-HFP) + 2.5 wt.% Mg 2 B 2 O 5 ] separator also provides discharge capacity retention of 99.9% after 100 cycles at 9 C, in comparison with only 87 % for polypropylene separator. Such results reveal that P(VdF-co-HFP) membrane containing 2.5 wt.% Mg 2 B 2 O 5 is a highly promising separator with good safety which can be used in high-performance lithium-ion batteries.

polymer science