Scalable synthesis of porous graphite/silicon@pitch carbon nanocomposites derived from wastes of silica fume for high-performance lithium storage

Bo Wang,Yue Li,Nan Wu,Kun Liu,Liujie Yin,Ziyi Han

DOI: https://doi.org/10.1039/d3nj01832f

IF: 3.3

2023-05-24

New Journal of Chemistry

Abstract:A novel porous pitch-pyrolyzed carbon coated spent graphite/silicon (SG/Si@C) nanocomposites was fabricated with a scalable and cost-effective method, including the processes of mechanical ball milling, spray-drying, and followed by simultaneously magnesiothermic reduction and carbonization processes. The spent graphite and silica fume were employed as the carbon and silicon sources, respectively. Another carbon source was directly deposited on the surface of the spent graphite/silicon particles by means of the carbonization of mesophase pitch. In this ingenious structure of composites, nano-Si particles are uniformly distributed and anchored on the surface of graphite via pitch-pyrolyzed carbon. The graphite in the composites provides sufficient electrical conductivity and mechanical strength for SG/Si@C nanocomposites, and the amorphous carbon coating layer pyrolyzed by mesophase pitch is beneficial for relieving the volume expansion of Si particles, stabilizing SEI passivation layers and inhibiting Si nanoparticles pulverization during the lithiation/delithiation process. Benefitting from this innovative approach and rational structural design, the as-prepared SG/Si@C nanocomposites electrode delivers a high initial reversible specific capacity of 903.69 mAh g-1 with an initial Coulombic efficiency of 82.34%, and the reversible capacity was maintained at 799.37 mAh g-1 over 500 cycles at current density of 200 mA g-1. On account of these aspects, the proposed rational design of pitch-pyrolyzed carbon coating for macro scale SG/Si structures, as well as low-cost raw materials are practical for implementation in commercial applications.

chemistry, multidisciplinary