Formation Mechanism of Nitrogen-Doped Titanium Monoxide Nanospheres and Their Application as Sulfur Hosts in Lithium Sulfur Batteries
Miaoran Li,Ying Zhu,Xiaodong Wu,Yimin Lei,Xuexia He,Qi Li,Ruibin Jiang,Zhibin Lei,Zonghuai Liu,Jie Sun
DOI: https://doi.org/10.1021/acsaem.1c00560
IF: 6.4
2021-06-17
ACS Applied Energy Materials
Abstract:Lithium–sulfur batteries are one of the most promising next generation electrochemical devices with low cost and high energy density. Up to now, various metal oxides with strong interaction with lithium polysulfides (LiPs) have been designed as sulfur hosts to inhibit the notorious shuttle effect. Nitrogen doping on metal oxides can not only improve their shortcomings of poor electrical conductivity, but also introduce additional oxygen vacancies to further enhance their interaction with LiPs. In this work, the nitrogen-doped titanium monoxide (N–TiO) nanospheres have been first synthesized through a one-step method based on the synergistic effect of carbothermal reduction and nitridation reaction. The X-ray diffraction results suggested the gradually changed diffraction peak position, corresponding to the nitridation process. Through the calculation of Gibbs free energies in the temperature range of 800–1500 K, it was confirmed that TiO<sub>2</sub> can directly transform to TiO and then to TiN. Moreover, the structural characterization and X-ray photoelectron spectroscopy results suggested the synthesized N–TiO nanospheres contain mixed valences of Ti<sup>4+</sup>, Ti<sup>3+</sup>, and Ti<sup>2+</sup>, together with a significantly increased O vacancy concentration. By using N–TiO/S as the cathode, a high initial capacitance of 1438 mA h g<sup>–1</sup> at 0.2 C can be achieved, which was higher than those of the undoped TiO/S and TiN/S electrodes. In addition, such a cathode also delivered an initial discharge capacity of 1105 mA h g<sup>–1</sup> at 2 C, and retained 474 mA h g<sup>–1</sup> after 800 cycles, corresponding to the capacity decay rate of 0.071% per cycle. The strong interaction between O vacancies in N–TiO and LiPs, which has been confirmed through visible adsorption experiment and cyclic voltammetry curves of the Li<sub>2</sub>S<sub>6</sub> symmetric cells, is the main reason for its excellent electrochemical performance. This work can provide new ideas for the preparation and application of N-doped metal oxide materials in the field of lithium–sulfur batteries.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaem.1c00560?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaem.1c00560</a>.Thermodynamic calculation methods; SEM images of the as synthesized TiO<sub>2</sub> nanospheres; STEM image and SEI of the PDA-coated TiO<sub>2</sub> nanospheres with corresponding EDX mapping scan results; SEM images of N-TiO without PDA coating; morphology and structural characterization results of TiN and Ar-TiO nanospheres; high-resolution SEI images of the three types of nanospheres; TGA curves and structural characterization results of N-TiO/S, Ar-TiO/S, and TiN/S cathodes; CV curves of the N-TiO/S electrode and Li<sub>2</sub>S<sub>6</sub> symmetric cells with the three types of nanospheres as electrodes; galvanostatic charge–discharge curves of the three electrodes; calculated integrated area and relative content of fitted peaks in XPS spectra; and constants involved in the calculation of Gibbs free energies(<a class="ext-link" href="/doi/suppl/10.1021/acsaem.1c00560/suppl_file/ae1c00560_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels