Precipitation control by W addition in aged heat-resistant austenitic 22Cr-25Ni steels and its effect on mechanical properties

Peng Li,Wang Jian,Xudong Fang,Chao Chen,Peide Han,Yuping Li

DOI: https://doi.org/10.1016/j.matchar.2022.111768

IF: 4.537

2022-04-01

Materials Characterization

Abstract:The effect of tungsten (W) on the precipitation and mechanical properties of 22Cr-25Ni austenitic heat-resistant steel during aging at 700 °C was systematically studied. The equilibrium phase diagrams of the steels containing 1.5 and 2.5 wt% W were calculated by thermodynamics software, and their microstructure was examined by SEM, XRD, and TEM. The results show that the coarsening rate of Cr23C6 precipitates at grain boundaries was significantly decreased, and Cu-rich phase and Z phase were uniformly distributed in intracrystalline regions of the steel when 2.5 wt% W were added during the aging process at 700 °C, compared to the addition of 1.5 wt% W. W atoms quickly diffused and accumulated, which led to 8.33 wt% W atoms diffused into Cr23C6 to form Cr23C6 which contains high W content (high W-Cr23C6) at the grain boundaries, the specific interface energy between Cr23C6 and austenite was reduced, and boundary binding strength was improved. In addition, the formation of nano-scale precipitate phases at grain boundaries by elements such as Cu and Nb were inhibited due to the formation of high W-Cr23C6 at these locations, which resulted in the increase and more even distribution of Cu-rich phase and Z phase within the grain. The stress concentration on the triple junctions caused by trapeziform Cr23C6 was decreased by plate-like high W-Cr23C6 precipitates resulting in increased ductility.

materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing