KOH-activated porous biochar with high specific surface area for adsorptive removal of chromium (VI) and naphthalene from water: Affecting factors, mechanisms and reusability exploration

Jianhua Qu,Yuxin Wang,Xue Tian,Zhao Jiang,Fengxia Deng,Yue Tao,Qun Jiang,Lei Wang,Ying Zhang

DOI: https://doi.org/10.1016/j.jhazmat.2020.123292

IF: 13.6

2021-01-01

Journal of Hazardous Materials

Abstract:<p>Herein, a high-performance porous biochar described as PBC_KOH was successfully synthesized by two-step pyrolysis of corn straw with chemical activation of KOH, and was employed for the elimination of Cr(VI) and naphthalene (NAP) from water. Benefiting from KOH activation, the PBC_KOH was found to possess huge specific surface area of 2183.80 m²/g and many well-developed micropores with average particle size of 2.75 nm and main pore diameters distribution from 1 to 2 nm. The PBC_KOH presented an excellent adsorption performance with a theoretical monolayer uptake of 116.97 mg/g for Cr(VI) and a heterogeneous adsorption capacity of 450.43 mg/g for NAP. The uptake equilibrium was attained within about 120 min for Cr(VI), while about 180 min for NAP following avrami fractional-order model, revealing the existence of multiple kinetics during the adsorption. The thermodynamic results showed that the uptake of both Cr(VI) and NAP occurred spontaneously (-Δ<em>G</em>°), while in an endothermic nature for Cr(VI) (+Δ<em>H</em>°) and an exothermic characteristic for NAP (-Δ<em>H</em>°) with different randomness. Furthermore, the PBC_KOH was believed to enhance the Cr(VI) adsorption mainly through the combination of electrostatic attraction, complexation, ion exchange and reduction action, while achieving the high NAP uptake by pore filling and π-π stacking interactions.</p>

environmental sciences,engineering, environmental

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to develop an efficient method to remove hexavalent chromium (Cr(VI)) and naphthalene (NAP) from water. These two substances have potential hazards to the environment and human health. Specifically, the researchers prepared porous biochar (PBC KOH) with a high specific surface area by activating corn stalks with potassium hydroxide (KOH) through a two - step method, and evaluated its adsorption performance for Cr(VI) and NAP, and explored the influencing factors, adsorption mechanisms and the possibility of material regeneration and reuse.

### Main research contents include:
1. **Material preparation**: Prepare PBC KOH by activating corn stalks with KOH through a two - step method.
2. **Material characterization**: The surface morphology, chemical properties and pore structure of PBC KOH were characterized in detail.
3. **Adsorption performance evaluation**: The adsorption performance of PBC KOH for Cr(VI) and NAP was systematically studied, including pH - dependence, kinetics, isotherm and thermodynamic analysis.
4. **Regeneration and reuse**: The desorption and regeneration ability of PBC KOH was investigated, and the adsorption mechanism was explored.

### Key findings:
- **High specific surface area**: PBC KOH has a specific surface area as high as 2183.80 m²/g, much higher than that of unactivated biochar.
- **Excellent adsorption performance**: The maximum adsorption capacity of PBC KOH for Cr(VI) is 116.97 mg/g, and for NAP is 450.43 mg/g.
- **Adsorption mechanism**: The adsorption of Cr(VI) is mainly achieved through charge attraction, complexation, ion exchange and reduction; while the adsorption of NAP is mainly achieved through pore filling and π - π stacking.
- **Thermodynamic analysis**: The adsorption process of Cr(VI) is endothermic, while the adsorption process of NAP is exothermic, indicating the difference in their adsorption mechanisms.

### Research significance:
This research not only provides an efficient water treatment material, but also provides new ideas for the resource utilization of agricultural wastes, which is helpful for environmental protection and sustainable development.