Preparation, crystal structure, and photoluminescence properties of high-brightness red-emitting Ca2LuNbO6:Eu3+ double-perovskite phosphors for high-CRI warm-white LEDs

Xiaoyong Huang,Qi Sun,Balaji Devakumar

DOI: https://doi.org/10.1016/j.jlumin.2020.117373

IF: 3.6

2020-09-01

Journal of Luminescence

Abstract:<p>Near-ultraviolet-excited efficient red phosphors are important for fabricating warm-white light-emitting diodes (LEDs) with high color rendering index. Herein, we demonstrated the preparation of novel highly efficient Eu³⁺ ions-activated Ca₂LuNbO₆ (CLN) double-perovskite phosphors. These phosphors were prepared by the high-temperature solid-state reaction method and they were characterized by powder X-ray diffraction, Rietveld refinement, excitation and emission spectra, decay lifetimes, internal quantum efficiency, and temperature-dependent emission spectra. The as-prepared phosphors can be efficiently excited by 396 nm near-ultraviolet light and generated bright red luminescence around 591, 616, 656 and 703 nm corresponding to the ⁵D₀→⁷F_J (J = 1–4) transitions of Eu³⁺ ions. The optimal doping concentration of CLN:xEu³⁺ (<em>x</em> = 0.2, 0.3, 0.4, 0.5, 0.6, 0.7, and 0.8) phosphors was <em>x</em> = 0.4, and the optimal CLN:0.4Eu³⁺ sample exhibited high-color-purity (96.4%) red emission with internal quantum efficiency as great as 66%. The thermal-quenching resistance was evaluated by measuring their temperature-dependent emission intensities, while the emission intensity at 150 °C was about 65% of that at room temperature. Finally, a warm white LED lamp was made by using a 395 nm LED chip together with a phosphor blend of commercial blue phosphor BaMgAl₁₀O₁₇:Eu²⁺ and commercial green phosphor (Ba,Sr)₂SiO₄:Eu²⁺ and newly developed red phosphor CLN:0.4Eu³⁺, which gave bright high-quality white light with Commission Internationale de l'Eclairage (CIE) chromaticity coordinates of (0.3878, 0.3725), a correlated color temperature of 3769 K, and a color rendering index of 94 when the driven current was 20 mA. These investigation results clearly revealed the promising application potential of CLN:Eu³⁺ red phosphors in high-color-quality solid-state white lighting.</p>

optics

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to develop a new - type and highly efficient red phosphor for manufacturing warm - white - light - emitting diodes (LEDs) with a high color - rendering index (CRI). Specifically, the research aims to synthesize a new europium ion (Eu³⁺) - activated Ca₂LuNbO₆ (CLN) double - perovskite phosphor. This phosphor can emit bright red light under near - ultraviolet light (396 nm) excitation and has high color purity and good thermal stability. By optimizing the doping concentration of europium ions, the researchers hope to find the best phosphor formula to achieve the highest luminous efficiency and the best optical performance, so as to meet the needs of solid - state lighting applications.

### Main research contents:
1. **Synthesis and characterization of phosphors**:
- Ca₂LuNbO₆:Eu³⁺ phosphors with different europium ion doping concentrations were prepared by the high - temperature solid - phase reaction method.
- The phosphors were characterized in detail by means of X - ray diffraction (XRD), Rietveld refinement, excitation and emission spectra, decay lifetime, internal quantum efficiency (IQE) and temperature - dependent emission spectra.

2. **Analysis of optical properties**:
- The photoluminescence (PL) and photoluminescence excitation (PLE) spectra of the phosphor under 396 nm near - ultraviolet light excitation were studied.
- The optimal doping concentration of europium ions was analyzed. It was found that when the doping concentration of europium ions was 0.4, the phosphor had the highest luminous intensity, the color purity reached 96.4%, and the internal quantum efficiency was as high as 66%.

3. **Evaluation of thermal stability**:
- The luminous intensity of the phosphor at different temperatures was measured to evaluate its thermal quenching performance. The results showed that even at a high temperature of 150 °C, the luminous intensity of the phosphor still remained about 65% of that at room temperature, showing good thermal stability.

4. **Verification of practical applications**:
- A warm - white - light LED lamp was fabricated, using a 395 nm near - ultraviolet LED chip, commercial blue - and green - light phosphors and the newly developed red - light phosphor CLN:0.4Eu³⁺. The test results showed that the CIE color coordinates of this LED lamp were (0.3878, 0.3725), the correlated color temperature was 3769 K, and the color - rendering index was 94, showing excellent optical performance.

### Conclusion:
Through the above research, the researchers successfully developed a new - type and highly efficient europium ion - activated Ca₂LuNbO₆ double - perovskite red phosphor. This phosphor has high brightness, high color purity and good thermal stability under near - ultraviolet light excitation and is suitable for solid - state white - light - lighting applications with high color - rendering quality. These results indicate that the CLN:Eu³⁺ phosphor has broad application prospects in the future LED - lighting field.