Characterizing Magnetic Skyrmion Ordering and Dis-Ordering in the Presence of Crystalline Dislocations using Lorentz Transmission Electron Microscopy
Reed Yalisove,Peter Meisenheimer,Hongrui Zhang,Rui Chen,Xiang Chen,Robert J Birgeneau,Jie Yao,Ramamoorthy Ramesh,Mary C Scott
DOI: https://doi.org/10.1093/micmic/ozad067.848
IF: 4.0991
2023-07-24
Microscopy and Microanalysis
Abstract:Topological spin textures, such as magnetic skyrmions, present a novel opportunity to study the relationship between atom-scale details and microscale ordering of spins. In Co-doped Fe 5 GeTe 2 (FCGT), a small change in Co concentration to exactly 50% causes a structural phase change allowing for ferromagnetism and the Dzyaloshinskii-Moriya interaction, leading to the appearance of magnetic Néel skyrmions [ 1]. Interactions between skyrmions and the surrounding crystal govern temperature- and magnetic field-dependent ordering [ 2]. These studies describe the long-range ordering of skyrmions, but do not elucidate the mechanics of skyrmion-skyrmion, skyrmion-crystal, or skyrmion-defect interactions. Lorentz transmission electron microscopy (LTEM) is a convenient technique to study magnetic textures under a range of magnetic field and temperature conditions, in the same tool that can measure crystalline defects on an atomic scale. Even without atomic resolution, crystalline defects such as dislocations are apparent in diffraction contrast. Here we investigate skyrmion ordering and dis-ordering in the presence of crystalline defects. LTEM images of skyrmions were taken by cooling FCGT in the TEM under a magnetic field applied by slightly exciting the objective lens. FCGT has Néel skyrmions, so the sample is tilted slightly in the microscope to create contrast. These skyrmions are clearly visible in Fig. 1a, along with several line defects in the crystal. These defects show clear diffraction contrast when imaging on-axis (0001) in conventional TEM mode (Fig. 1b). Tilting the sample into a two-beam condition (Fig. 1c,d) causes certain sets of these defects to become invisible, suggesting that they are dislocations in the crystal lattice. Here we see that various dislocations have Burgers' vector in the [1-210] directions (Fig 1c) and or the [03-30] directions. LTEM can image both skyrmions and dislocations in the crystal lattice, allowing us to probe the interactions between skyrmions and crystalline defects and the effects on ordering.
materials science, multidisciplinary,microscopy