Facile Preparation of Continuous and Porous Polyimide Aerogel Fibers for Multifunctional Applications
Mengmeng Li,Feng Gan,Jie Dong,Yuting Fang,Xin Zhao,Qinghua Zhang
DOI: https://doi.org/10.1021/acsami.0c21842
2021-02-17
Abstract:High-performance aerogel fibers with high porosity, ultralow density and thermal conductivity, and good flexibility are attractive candidates for the next generation of effective thermal insulation, efficient personal thermal management, and other functional applications. However, most previously reported aerogel fibers suffered from either limited working temperatures, weak mechanical properties, or complex manufacturing processes. In the present work, a facile wet-spinning technique combined with freeze-drying was developed to fabricate strong polyimide aerogel fibers (PAFs) based on organo-soluble polyimide. Attributed to the unique "porous core–dense sheath" morphology, the PAFs exhibited excellent mechanical properties with an optimum tensile strength of 265 MPa and an initial modulus of 7.9 GPa at an ultimate elongation of 65%, representing the highest value for aerogel fibers reported so far. Moreover, the PAFs possess high porosity (>80%) and high specific surface area (464 m<sup>2</sup> g<sup>–1</sup>), which render the woven PAF fabrics with excellent thermal insulation properties within a wide temperature range (−190 to 320 °C) and potential applications for thermal insulation under harsh environments. Additionally, a series of functionalized aerogel fibers or their fabrics based on PAFs, including phase-change fabrics with a thermoregulation function and electromagnetic shielding (EMI) textiles with a high EMI SE value, have been successfully fabricated for expanding their potential applications. Overall, this novel aerogel fiber sheds light on a promising direction for developing the next generation of high-performance thermal insulation and multifunctional fibers and textiles.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c21842?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c21842</a>.Optical images of the prepared PAF and woven textile, cross-sectional SEM images with different magnifications of the PAFs, cross-sectional SEM image of the PI fiber, nitrogen adsorption/desorption isotherms and the pore size distribution of PAFs, small-angle X-ray scattering of PAF measured at different strains, initial cross-sectional morphology and fractured morphology after the tensile test of PAF-5, TGA and DTG curves of PAF with PEG-1000 and stearic acid, and XRD and XPS wide-scan spectra of pristine PAF and AgNP-deposited PAF fibers (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c21842/suppl_file/am0c21842_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology