Magnetoelectric Response in Multiferroic SrFe12O19 Ceramics

Guolong Tan,Yao Huang,Haohao Sheng
DOI: https://doi.org/10.1371/journal.pone.0167084
2016-09-15
Abstract:We report here the realization of ferroelectricity, ferromagnetism and magnetocapacitance effect in SrFe12O19 ceramics at room temperature. The ceramics demonstrate a saturated polarization hysteresis loop, two I-V peaks and large anomaly of dielectric constant near Curie temperature. These evidences confirmed the ferroelectricity of SrFe12O19 ceramics after annealing in O2 atmosphere. The remnant polarization of the SrFe12O19 ceramic is 103 {\mu}C/cm2. The material also exhibits strong ferromagnetic characterization, the coercive field and remnant magnetic moment are 6192Oe and 35.8emu/g, respectively. Subsequent annealing SrFe12O19 ceramics in O2 not only reveals its innate ferroelectricity but also improves the ferromagnetic properties through transforming Fe2+ into Fe3+. By applying a magnetic field, the capacitance demonstrates remarkable change along with B field, the maximum relative change of dielectric constant is 1174%, which reflects a giant magnetocapacitance effect in SrFe12O19. These combined functional responses in SrFe12O19 ceramics opens substantial possibilities for applications in novel electric devices.
Materials Science
What problem does this paper attempt to address?
The problem that this paper attempts to solve is: How to optimize the preparation process at room temperature so that SrFe\(_{12}\)O\(_{19}\) ceramics can simultaneously exhibit significant ferroelectricity and strong ferromagnetism, and achieve a huge magnetocapacitance effect. Specifically, the author hopes to solve the problem through the following points: 1. **Improve ferroelectric properties**: By annealing in an oxygen atmosphere, oxygen vacancies are removed and Fe\(^{2+}\) is converted to Fe\(^{3+}\), thereby reducing current leakage and obtaining a saturated ferroelectric hysteresis loop and significant remanent polarization. 2. **Enhance ferromagnetic properties**: Through the same oxygen annealing treatment, Fe\(^{2+}\) is converted to Fe\(^{3+}\), increasing the unpaired electron spin, thereby increasing the coercive field and remanent magnetic moment of the material. 3. **Achieve a huge magnetocapacitance effect**: By applying a magnetic field, a huge response of capacitance to the change of magnetic field is observed, verifying the magnetoelectric coupling characteristics of the material. ### Specific problem description #### 1. Ferroelectricity - **Background problem**: In previous studies, the ferroelectricity of SrFe\(_{12}\)O\(_{19}\) has been controversial, especially the "banana - shaped" P - E hysteresis loop exhibited in single - crystal samples, which may be caused by the leakage current due to oxygen vacancies and Fe\(^{2+}\). - **Solution**: By annealing in an oxygen atmosphere, oxygen vacancies are removed and Fe\(^{2+}\) is converted to Fe\(^{3+}\), which greatly increases the resistivity and reduces the leakage current, thereby obtaining a saturated ferroelectric hysteresis loop. The experimental results show that the remanent polarization value reaches 103 μC/cm\(^2\), much higher than that of the untreated sample (15 μC/cm\(^2\)). #### 2. Ferromagnetism - **Background problem**: Although the ferromagnetism of SrFe\(_{12}\)O\(_{19}\) is relatively strong, in the case of insufficient oxygen content, the presence of Fe\(^{2+}\) will reduce its magnetism. - **Solution**: Through oxygen annealing, Fe\(^{2+}\) is converted to Fe\(^{3+}\), increasing the unpaired electron spin, thereby increasing the coercive field (from 4111 Oe to 6192 Oe) and the remanent magnetic moment (from 33.5 emu/g to 35.8 emu/g). #### 3. Magnetocapacitance effect - **Background problem**: Some materials can exhibit magnetoelectric coupling effects under specific conditions, but the magnetocapacitance effect of SrFe\(_{12}\)O\(_{19}\) has not been fully studied. - **Solution**: By measuring the change of capacitance with the magnetic field, it is found that SrFe\(_{12}\)O\(_{19}\) exhibits a significant magnetocapacitance effect under the action of the magnetic field, and the maximum relative change reaches 1174%, indicating that this material has great potential for magnetoelectric coupling. ### Summary This paper successfully realizes the synchronous enhancement of ferroelectricity and ferromagnetism of SrFe\(_{12}\)O\(_{19}\) ceramics at room temperature by optimizing the preparation process, and shows a huge magnetocapacitance effect. These results provide the possibility for the development of new multi - functional electronic devices.