Abstract:Nanometric voids are one of the fundamental defects generated by neutron irradiation in fusion environment, which impede dislocation motion and cause hardening of plasma facing tungsten. Accurate prediction of voids hardening is crucial for safety evaluation of irradiated tungsten. In this paper, we develop a void-dislocation interaction model within the framework of dislocation dynamics (DD) and implement it in open-source DD software ParaDiS. We use this model to study the hardening effects of randomly-distributed voids with different sizes and number densities. The model for short-range interaction during dislocation-void contact, especially the dislocation movement on void surface, is informed and calibrated by atomistic simulations. Meanwhile, the long-range elastic interaction between dislocation and void is efficiently computed by the approach developed in our recent work (Wu et al., 2022) with Eshelby's equivalent inclusion method. Our DD simulations show that the average resistance by voids with various sizes is proportional to the 2/3 power of total number density. We also find that a modified Friedel-Kroupa-Hirsch (MFKH) model can quantify the hardening effects of nanometric voids, where the hardening coefficient depends on an effective average void diameter that accounts for the size distribution of voids. This MFKH model extends our previous work (Wu et al., 2022) that addresses the hardening of small vacancy clusters where dislocations simply cut through them, which is essentially an elastic perturbation to the dislocation dynamics. The proposed MFKH model can predict both small vacancy clusters and nanometric voids hardening effects with only difference in size dependent hardening coefficient. We further verify the MFKH model by comparing its quick predictions of the hardening effects by randomly-distributed nanometric voids with experiments on twelve neutron-irradiated tungsten samples.

Object Kinetic Monte Carlo Simulations of Radiation Damage in Bulk Tungsten Part-II: With a PKA Spectrum Corresponding to 14-MeV Neutrons

Object Kinetic Monte Carlo Simulations of Radiation Damage in Neutron-Irradiated Tungsten Part-I: Neutron Flux with a PKA Spectrum Corresponding to the High-flux Isotope Reactor

Dose rate effects on damage accumulation and void growth in self-ion irradiated tungsten

Initial microstructure and temperature dependence of irradiation defects evolution in tungsten

High-dose long-time defect evolution in tungsten studied by atomistically informed Object Kinetic Monte Carlo simulations

Displacement cascade evolution in tungsten with pre-existing helium and hydrogen clusters: a molecular dynamics study

Primary radiation damage near grain boundary in bcc tungsten by molecular dynamics simulations

The Evolution of Structural Defects under Irradiation in W by Molecular Dynamics Simulation

Effect of dose rate on dislocation loop evolution in tungsten: Combination of defect generation rate and elastic interaction

On the classification and quantification of crystal defects after energetic bombardment by machine learned molecular dynamics simulations

Temperature effects on the point defects formation in [111] W by neutron induced collision cascade

Electronic Energy Loss Assessment in Theoretical Modeling of Primary Radiation Damage in Tungsten

Positron lifetime study of ion-irradiated tungsten: Ion type and dose effects

Effect of Radiation Defects on Grain Boundary Evolution under Shock Loading

Long-term microstructural evolution of tungsten under heat and neutron loads

Modified deformation behaviour of self-ion irradiated tungsten: A combined nano-indentation, HR-EBSD and crystal plasticity study

Molecular dynamics simulations of the defect evolution in tungsten on successive collision cascades

Defect annealing in heavy-ion irradiated tungsten: Long-time thermal evolution of saturated displacement damage at different temperatures

Deuterium retention and transport in ion-irradiated tungsten exposed to deuterium atoms: role of grain boundaries

Atomically-informed dislocation dynamics model for prediction of void hardening in irradiated tungsten

Electronic effects in high-energy radiation damage in tungsten