Charge state dynamics of the nitrogen vacancy center in diamond under 1064 nm laser excitation

Peng Ji,M. V. Gurudev Dutt

DOI: https://doi.org/10.1103/PhysRevB.94.024101

2016-04-07

Abstract:The photophysics and charge state dynamics of the nitrogen vacancy (NV) center in diamond has been extensively investigated but is still not fully understood. In contrast to previous work, we find that NV$^{0}$ converts to NV$^{-}$ under excitation with low power near-infrared (1064 nm) light, resulting in $increased$ photoluminescence from the NV$^{-}$ state. We used a combination of spectral and time-resolved photoluminescence experiments and rate-equation modeling to conclude that NV$^{0}$ converts to NV$^{-}$ via absorption of 1064 nm photons from the valence band of diamond. We report fast quenching and recovery of the photoluminescence from $both$ charge states of the NV center under low power 1064 nm laser excitation, which has not been previously observed. We also find, using optically detected magnetic resonance experiments, that the charge transfer process mediated by the 1064 nm laser is spin-dependent.

Materials Science

What problem does this paper attempt to address?

This paper aims to address the optoelectronic properties of nitrogen - vacancy (NV) centers in diamond and the dynamics of their charge states. Specifically, the authors found that under low - power near - infrared (1064 nm) photo - excitation, the neutral nitrogen - vacancy center (NV0) can be converted into the negatively - charged nitrogen - vacancy center (NV−), a process that leads to the enhancement of the photoluminescence of the NV− state. In addition, the study also revealed the rapid quenching and recovery of photoluminescence in both charge states, which had not been observed before. Through optically - detected magnetic resonance experiments, the authors further found that the 1064 - nm - laser - mediated charge - transfer process is spin - dependent.

### Main problems and findings
1. **Charge - state conversion**:
- The study found that under low - power excitation of 1064 - nm near - infrared light, NV0 can be converted into NV−, thereby enhancing the photoluminescence of NV−.
- Through spectroscopic and time - resolved photoluminescence experiments and rate - equation modeling, the authors concluded that NV0 is converted into NV− by absorbing 1064 - nm photons and capturing electrons from the valence band of diamond.

2. **Rapid quenching and recovery**:
- It was observed that under low - power 1064 - nm laser excitation, the photoluminescence of both charge states exhibited rapid quenching and recovery, which had not been reported in previous literature.
- The time scale of rapid quenching and recovery is on the order of nanoseconds, while the slow charge - transfer time scale is on the order of microseconds.

3. **Spin - dependence**:
- Through optically - detected magnetic resonance experiments, the authors found that the 1064 - nm - laser - mediated charge - transfer process is spin - dependent. In particular, when NV− is in the |ms = ±1⟩ state, it is more likely to convert NV0 into NV−.

### Experimental methods
- **Sample preparation**: High - purity diamond samples were used, and NV centers were prepared by nitrogen - ion implantation and annealing treatment.
- **Experimental setup**: A confocal microscope system was constructed, combining 532 - nm and 1064 - nm lasers for imaging and exciting NV centers.
- **Data collection**: Photoluminescence signals were collected through a single - photon - counting module (SPCM) and a spectrometer, and different band - pass filters were applied to distinguish the photoluminescence of NV− and NV0.

### Conclusion
Through experimental and theoretical analysis, the authors revealed the charge - state dynamics of NV centers under 1064 - nm near - infrared light excitation, including rapid quenching and recovery phenomena and spin - dependence. These findings are of great significance for understanding the optoelectronic properties of NV centers and their applications in fields such as quantum information, nano - scale magnetic - field and electric - field sensing.