Self-Neutralizing Melamine–Urea–Formaldehyde–Citric Acid Resins for Wood Panel Adhesives

Xuedong Xi,Antonio Pizzi,Hong Lei,Xiaojian Zhou,Guanben Du
DOI: https://doi.org/10.3390/polym16131819
IF: 5
2024-06-28
Polymers
Abstract:In this study, we used a self-neutralizing system to counteract too acidic a pH, unsuitable for wood adhesives, and tested it on MUF resins augmented by the addition of citric acid or other organic acids, based on the addition of small percentages of hexamine or another suitable organic base to form an acid–base buffer. In this manner, the pH of the adhesive was maintained above the minimum allowed value of 4, and the strength results of wood particleboard and plywood bonded with this adhesive system increased due to the additional cross-linking imparted by the citric acid. Thus, the wood constituents at the wood/adhesive interface were not damaged/degraded by too low a pH, thus avoiding longer-term service failure of the bonded joints. The addition of the buffering system increased the strength of the bondline in both the plywood and particleboard, both when dry and after hot water and boiling water tests. The IB strength of the particleboard was then increased by 15–17% when dry but by 82% after boiling. For the plywood, the shear strengths when dry and after 3 h in hot water at 63 °C were, respectively, 37% and 90% higher than for the control. The improvement in the bonded panel strength is ascribed to multiple reasons: (i) the slower, more regular cross-linking rate due to the action of the buffer; (ii) the shift in the polycondensation–degradation equilibrium to the left induced by the higher pH and the long-term stability of the organic buffer; (iii) the additional cross-linking by citric acid of some of the MUF resin amine groups; (iv) the already known direct linking of citric acid with the carbohydrates and lignin constituents at the interface of the wood substrate; and (v) the likely covalent linking to the interfacial wood constituents of the prelinked MUF–citric acid resin by some of the unreacted citric acid carboxyl groups.
polymer science
What problem does this paper attempt to address?
The problem that this paper attempts to solve is that when citric acid is used as a modifier in wood - product adhesives, its strong acidity may cause damage to wood. Specifically, in traditional wood - product adhesives such as melamine - urea - formaldehyde (MUF) resin, after adding citric acid, although the performance is improved, the too - low pH value (usually less than 4) will lead to the degradation of wood, thereby affecting the bonding strength and the long - term stability of the product. To solve this problem, researchers proposed a self - neutralizing system. By adding a small amount of hexamine or other suitable organic bases to the MUF - citric acid resin to form an acid - base buffer system, the pH value of the adhesive can be maintained within an appropriate range, avoiding damage to the wood and improving the bonding strength and water resistance of wood products. ### Research Background 1. **Application of Citric Acid** - As a natural product, citric acid shows great potential in the application of wood - product adhesives and can significantly improve the performance of adhesives, especially in improving water solubility and water resistance. - However, the strong acidity of citric acid (the pH value is usually between 0.8 and 2) has a corrosive effect on wood, which does not meet the requirements of most global wood - product bonding standards. These standards stipulate that adhesives with a pH value lower than 4 cannot be used for wood. 2. **Deficiencies of Traditional Solutions** - Although previous studies have proposed solving the strong acidity problem of citric acid through self - neutralizing systems, these methods are mainly applicable to starch - citric acid adhesives and cannot be directly applied to traditional synthetic adhesives. - Therefore, it is necessary to develop a new and simpler system that can improve the performance of traditional adhesives using citric acid without damaging the wood. ### Research Purposes - **Develop a Self - Neutralizing System**: By adding a small amount of hexamine to the MUF - citric acid resin to form an acid - base buffer system, maintain the pH value of the adhesive above 4 and avoid damage to the wood. - **Improve Bonding Performance**: Through experimental verification, the application of this self - neutralizing system can significantly improve the dry - state and wet - state bonding strengths of wood particle boards and plywood, especially the performance after hot water and boiling water tests. ### Experimental Methods - **Preparation of MUF Resin**: Prepare MUF resin in the laboratory. The detailed steps include adjusting the pH value, adding urea and melamine, and controlling the reaction temperature, etc. - **Test of Buffer Action**: Through titration experiments, test the buffer effects of different proportions of hexamine on MUF - citric acid resin and MUF - p - toluenesulfonic acid resin. - **Performance Test**: Prepare and test the bonding strengths of wood particle boards and plywood of MUF resin added with citric acid and hexamine, including the performance in dry and wet states. ### Results and Discussion - **Buffer Effect**: The experimental results show that adding 3.3% hexamine can significantly increase the pH value of MUF - citric acid resin, keep it above 4, and effectively avoid the degradation of wood. - **Bonding Performance**: The bonding strengths of wood particle boards and plywood made of MUF - citric acid resin using the self - neutralizing system are significantly improved, especially in wet - state conditions, and the performance improvement is more obvious. - **Mechanism Analysis**: Through nuclear magnetic resonance (NMR) and matrix - assisted laser desorption ionization - time - of - flight mass spectrometry (MALDI - TOF), the reaction mechanism between citric acid and MUF resin was studied, confirming the cross - linking effect of citric acid in the resin and the effectiveness of the buffer system. ### Conclusions - By introducing the self - neutralizing system formed by hexamine, the strong acidity problem of MUF - citric acid resin has been successfully solved, which not only improves the bonding strength of wood products but also ensures the long - term stability of the products. - This method provides an effective solution for using citric acid to improve traditional adhesives and has important industrial application prospects.