Abstract:The particle size and pore size of spherical mesoporous silica materials play significant roles in their application. However, relatively limited systematic research has been conducted on how preparation conditions influence these properties. In particular, the effects of some important factors have not been adequately studied, including reaction time, reaction temperature, and organic solvent type. In this work, octane and water were used as solvents, and tetraethyl orthosilicate was used as the silicon source to systematically study the effects of reaction time, reaction temperature, different organic solvents, octane/water mass ratio, styrene template concentration, and surfactant (cetyltrimethylammonium bromide, CTAB)/H2O mass ratio on the particle morphology, particle size, and pore size of silica. The results suggest that the above-mentioned neglected factors exert a substantial influence on both particle size and pore size. In the experimental temperature range, the pore diameter decreases and the particle size increases with increasing temperature. The maximum particle size and pore size are achieved after a reaction time of 3 h, and a further increase in reaction time leads to a smaller particle size and pore size. As the number of carbon atoms in the organic solvent decreases, the pore size also gradually increases. Styrene and organic solvents that dissolve in CTAB micelles are crucial factors in pore formation, while the aggregation of the swollen CTAB micelles influences the particle size. The changes in the pore structure stability and hydroxyl density of the synthesized samples in water were also studied. After undergoing water treatment at temperatures ranging from 20 to 60 °C for 72 h, both the pore structure and morphology remain relatively unchanged. When the temperature increases, the surface hydroxyl density exhibits a more pronounced increase in the presence of water. After water treatment for 5 h, the surface hydroxyl density reaches saturation.

Synthesis of mesoporous carbon particles with different pore sizes by soft template method

Preparation of cage-like nano-CaCO3 hollow spheres for enhanced CO2 sorption

Electron Microscopy and Nitrogen Adsorption Studies of Film-Type Carbon Replicas with Large Pore Volume Synthesized by Using Colloidal Silica and Sba-15 As Templates

Facile Synthesis of MOF-5-derived Porous Carbon with Adjustable Pore Size for CO2 Capture

Mesoporous Carbon Materials: Synthesis and Modification.

Tetraethyl orthosilicate-assisted synthesis of nitrogen-containing porous carbon spheres

A Simple Method for the Synthesis of High Surface Area Mesoporous Carbon Monolith via Soft Template Technique

Synthesis of Ordered Mesoporous Silica with Tunable Morphologies and Pore Sizes Via a Nonpolar Solvent-Assisted Stöber Method

Preparation of mesoporous carbon with adjustable diameter and pore size

A Facile Soft-Template Synthesis of Mesoporous Polymeric and Carbonaceous Nanospheres

Synthesis of mesoporous silica particles with controlled pore structure

Effects of synthesis conditions on particle size and pore size of spherical mesoporous silica

Doped Porous Carbon Spheres with Controllable Vesicle Structure: Preparation and the Effects of Pore Size on Electromagnetic Wave Absorption Properties

Bimodal Mesoporous Carbon Spheres with Small and Ultra-Large Pores Fabricated Using Amphiphilic Brush Block Copolymer Micelle Templates

Facile Synthesis of Hierarchically Porous Carbons from Dual Colloidal Crystal/Block Copolymer Template Approach

Synthesis of Ordered Mesoporous Silica Spheres with Controllable Diameter in Micrometer

The Synthesis of Porous Materials with Macroscopically Oriented Mesopores Interconnected by Branched Mesopores

Synthesis and Characterization of Small Pore Thick-Walled SBA-16 Templated by Oligomeric Surfactant with Ultra-Long Hydrophilic Chains

Chemical reaction kinetics-guided size and pore structure tuning strategy for fabricating hollow carbon spheres and their selective adsorption properties

Delicately Controlled Synthesis of Mesoporous Carbon Materials with Thin Pore Walls

Versatile Nanoemulsion Assembly Approach to Synthesize Functional Mesoporous Carbon Nanospheres with Tunable Pore Sizes and Architectures.