In vitro Studies of Titanium Alloy Discs Fabricated with Electron Beam Melting for Improving Transdermal Osseointegrated Implant Surfaces.

J. Springer

2010-08-12

Abstract:SPRINGER, JESSICA COLLINS. In vitro Studies of Titanium Alloy Discs Fabricated with Electron Beam Melting for Improving Transdermal Osseointegrated Implant Surfaces. (Under the direction of Dr. Ola Harrysson and Dr. Denis Marcellin‐Little). Custom (patient‐specific) transdermal osseointegrated implants generated using direct metal fabrication methods, such as electron beam melting (EBM) may be considered as alternatives to socket prostheses due to the more natural transfer of loads. EBM may be used to make metal implants that usually have polished solid surfaces and unpolished porous surfaces. The resistance to bacterial infection is critically important to the overall success of the procedure and may be improved with skin ingrowth at the skin‐implant interface. Human adipose‐derived adult stem cells (hASCs), normal human epidermal keratinocytes (NHEK), and neonatal normal human dermal fibroblasts (NHDF‐Neo) attach and proliferate when in contact with titanium, but that bond is likely influenced by the surface characteristics of the titanium implants. The in vitro biocompatibility of EBM Ti6Al4V structures were assessed by comparing the response of several types of cells to Ti6Al4V discs; solid polished EBM, solid unpolished EBM, porous EBM, and commercially produced. Chemical etching with a hydrofluoric‐nitric acid solution was also used as a method for reducing the surface roughness of EBM porous surfaces and the biocompatibility of these surfaces compared with NHDF‐Neo and NHEK cells. A transdermal osseointegrated implantable device was designed to enable future in vivo research of these surfaces. EBM and commercially produced Ti6Al4V discs were seeded with hASCs and assessed for cell proliferation, viability, and release of the proinflammatory cytokines interleukin‐6 (IL‐6) and interleukin‐8 (IL‐8). Cell proliferation was assessed using alamarBlue® assays at days 0, 1, 2, 3, and 7. Cell viability was assessed with LIVE/DEAD® staining on day 8. Additional discs were seeded with NHDF‐Neo or NHEK cells and assessed for cell proliferation at days 2 and 7 using alamarBlue® assays. Cell viability was analyzed with fluorescence‐based LIVE/DEAD® assays at days 7 and 8 for the NHDF‐Neo and NHEK, respectively. Porous etched and non‐etched discs were seeded with NHDF‐Neo or NHEK cells and cell proliferation, viability, and morphology were assessed. Cell proliferation was assessed on days 0, 2, and 7 using alamarBlue® assays. Cell viability was assessed on day 9 using LIVE/DEAD assays. Cell morphology was assessed with scanning electron microscopy (SEM) on day 8. The hASCs were alive on all discs after 8 days. Cellular proliferation on porous EBM discs was increased when compared to discs made of commercial Ti6Al4V, solid polished, and unpolished EBM discs. IL‐6 and IL‐8 releases at day 7 were lower for porous EBM discs than for other discs. Solid polished, unpolished, and porous EBM Ti6Al4V discs exhibited an acceptable biocompatibility profile compared to solid Ti6Al4V discs from a commercial source. For both NHDF‐Neo and NHEK cells, day 7 proliferation levels were higher for scaffolds with lower surface roughness values. No statistical difference was present between commercial and EBM‐fabricated titanium seeded with NHDF‐Neo cells. NHDF‐Neo cellular proliferation on etched EBM discs was increased compared to non‐etched discs. There was no difference in NHEK cellular proliferation between etched and non‐etched EBM discs. EBM is a valid option for the fabrication of custom orthopedic implants. For transdermal osseointegrated implants, the EBM etched surfaces appear to be an acceptable skin‐implant interface option. The EBM as‐processed surface may be successful for promoting bone ingrowth. To analyze these results in vivo, the transdermal osseointegrated implantable device can be fabricated with EBM and surgically implanted. The ability to efficiently create a porous ingrowth surface on custom implants is possible with EBM and these custom implants may restore mobility to many patients with amputated limbs. In vitro Studies of Titanium Alloy Discs Fabricated with Electron Beam Melting for Improving Transdermal Osseointegrated Implant Surfaces by Jessica Collins Springer A dissertation submitted to the Graduate Faculty of North Carolina State University in partial fulfillment of the requirements for the Degree of Doctor of Philosophy Industrial Engineering Raleigh, North Carolina 2010 APPROVED BY: __________________________________ __________________________________ Dr. Ola Harrysson Dr. Denis Marcellin‐Little Chair of Advisory Committee Co‐Chair of Advisory Committee __________________________________ __________________________________ Dr. Harvey West, II Dr. Denis Cormier __________________________________ Dr. Elizabeth Loboa

Engineering,Medicine,Materials Science