Antiferrodistortive Phase Transition in Pseudorhombohedral (Pb0.94Sr0.06)(Zr0.550Ti0.450)O3 : A Combined Synchrotron x-ray and Neutron Powder Diffraction Study

Ravindra Singh Solanki,S. K. Mishra,Anatoliy Senyshyn,I. Ishii,Chikako Moriyoshi,Takashi Suzuki,Yoshihiro Kuroiwa,Dhananjai Pandey

DOI: https://doi.org/10.1103/PhysRevB.86.174117

2014-03-21

Abstract:The controversies about the structure of the true ground state of pseudorhombohedral compositions of Pb(ZrxTi1-x)O3 (PZT) are addressed using a 6% Sr2+ substituted sample with x=0.550. Sound velocity measurements reveal a phase transition at Tc~279K. The temperature dependence of FWHM of (h00)pc peaks and the unit cell volume also show anomalies around 279K even though there is no indication of any change of space group in the synchrotron X-ray powder diffraction (SXRD) patterns. The neutron powder diffraction patterns reveal appearance of superlattice peaks below Tc~279K confirming the existence of an antiferrodistortive phase transition. The Rietveld analysis of the room temperature and low temperature SXRD data below Tc shows that the structure corresponds to single monoclinic phase in the Cm space group while the analysis of neutron powder diffraction data reveals that the structure of the ground state phase below Tc corresponds to the Cc space group. Our analysis shows that the structural models for the ground state phase based on R3c space group with or without the coexistence of the room temperature monoclinic phase in the Cm space group can be rejected.

Materials Science

What problem does this paper attempt to address?

The problem that this paper attempts to solve is the controversy over the real ground - state structure of lead zirconate titanate (PZT) materials under specific compositions, especially the determination of their space groups. Specifically, the research focuses on the following issues:

1. **Structural Controversy**: For PZT materials with a pseudo - orthorhombic monoclinic crystal system, especially (Pb₀․₉₄Sr₀․₀₆)(Zr₀․₅₅Ti₀․₄₅)O₃ (PSZT550) with 6% Sr²⁺ substitution, is the real ground - state space group at low temperatures R3c or Cc? This issue is controversial in the literature, and different research teams have proposed different models.

2. **Phase - transition Properties**: The research aims to confirm whether there is an antiferroelectric distortion (AFD) phase - transition and determine its phase - transition temperature and properties. Through a variety of experimental methods (such as synchrotron radiation X - ray diffraction, neutron powder diffraction, and elastic modulus measurement), the AFD phase - transition that occurs at about 279K and its impact on the crystal structure have been verified.

3. **Existence of Superlattice Phases**: The research also explores whether a superlattice phase is formed after the AFD phase - transition and confirms this by observing the appearance of superlattice peaks. The existence or non - existence of these superlattice peaks is directly related to the choice of structural model.

### Main Conclusions
Through a series of experiments and analyses, the authors have drawn the following conclusions:
- For PSZT550 with a pseudo - orthorhombic monoclinic crystal system, an AFD phase - transition does occur at low temperatures, and the phase - transition temperature is approximately 279K.
- The ground - state structure at low temperatures belongs to the Cc space group, rather than the traditional R3c space group. This conclusion has been confirmed through Rietveld refinement and the analysis of superlattice peaks.
- The AFD phase - transition causes the antiphasic tilting of oxygen octahedra, forming a superlattice structure, but these superlattice peaks are not visible in synchrotron radiation X - ray diffraction, but can be observed in neutron powder diffraction.

### Method Overview
- **Sample Preparation**: High - purity PSZT550 samples were prepared by the semi - wet method.
- **Experimental Methods**:
- Synchrotron radiation X - ray diffraction (SXRD)
- Neutron powder diffraction (NPD)
- Elastic modulus measurement (by ultrasonic velocity measurement)

Through these methods, the authors not only confirmed the existence of the AFD phase - transition but also accurately determined the low - temperature structural model, resolving the long - standing space - group controversy.