Absence of Tetragonal Distortion in (1-x)SrTiO3-xBi(Zn1/2Ti1/2)O3 Solid Solution

Rishikesh Pandey,Ravi Kiran Pillutla,Uma Shankar,Akhilesh Kumar Singh

DOI: https://doi.org/10.1063/1.4804934

2013-11-15

Abstract:We have carried out powder x-ray diffraction and dielectric studies on the lead free solid solution (1-x)SrTiO3-xBi(Zn1/2Ti1/2)O3 ((1-x)ST-xBZT) with x=0.05, 0.10, 0.15, 0.20, 0.30 and 0.50 to explore the ferroelectric and piezoelectric properties. Analysis of the powder x-ray diffraction data reveals the cubic structure (space group Pm3m) of (1-x)ST-xBZT for the composition with x < 0.20, at room temperature as well as at low temperature. Highly tetragonal BZT fails to introduce any tetragonality when alloyed with ST. The solid solubility is limited to x< 0.20 and for higher BZT concentrations impurity phases start appearing. The ferroelectric and dielectric characterization of (1- x)ST-xBZT solid solution shows that all the compositions are paraelectric. The implications of the absence of tetragonal distortion in (1-x)ST-xBZT solid solution is discussed in connection with recently investigated other solid solutions based on BZT.

Materials Science

What problem does this paper attempt to address?

The main problem that this paper attempts to solve is to explore whether in the (1 - x)SrTiO₃ - xBi(Zn₁/₂Ti₁/₂)O₃ (abbreviated as (1 - x)ST - xBZT) solid solution, tetragonal distortion can be introduced by doping Bi(Zn₁/₂Ti₁/₂)O₃ (BZT), thereby developing lead - free ferroelectric materials with high piezoelectric response.

Specifically, the researchers hope to solve the problem through the following aspects:

1. **Structural analysis**: The crystal structures of (1 - x)ST - xBZT solid solutions with different BZT concentrations (x = 0.05, 0.10, 0.15, 0.20, 0.30 and 0.50) were studied by powder X - ray diffraction (XRD). The results show that at room temperature and low temperature, for samples with x ≤ 0.20, the structure remains cubic phase (space group Pm3m), while higher BZT concentrations will lead to the appearance of impurity phases.

2. **Dielectric and ferroelectric properties**: The dielectric constant and polarization - electric field (P - E) loops of (1 - x)ST - xBZT solid solutions with different BZT concentrations were studied. The results show that all components are paraelectric phases, and no ferroelectric behavior or tetragonal distortion was observed.

3. **Microstructural analysis**: The microstructures of samples with different BZT concentrations were observed by scanning electron microscopy (SEM). The results show that with the increase of BZT concentration, two different grain morphologies appear, which are consistent with the impurities found in XRD analysis.

4. **Low - temperature XRD study**: In order to verify whether a phase transition will occur at low temperature, the researchers carried out low - temperature XRD tests on samples with x = 0.10. The results show that even at 13 K, the structure is still cubic phase and no phase transition occurs.

In summary, this paper aims to explore whether BZT can be used as a tetragonal - phase component to replace PbTiO₃ (PT) for developing lead - free ferroelectric materials. However, the experimental results show that BZT cannot introduce tetragonal distortion, but instead leads to the formation of impurity phases at higher concentrations. Therefore, BZT is not an ideal candidate material for developing lead - free ferroelectric materials with high piezoelectric response.

### Key formulas
- Space group: Pm3m
- Lattice parameters: \( a \) = 3.90516 Å (x = 0.05), \( a \) = 3.90764 Å (x = 0.10), \( a \) = 3.90932 Å (x = 0.15), \( a \) = 3.90952 Å (x = 0.20)
- Ti - O bond length: 1.9528 Å (0.9ST - 0.1BZT)

These results indicate that although BZT itself has a relatively high tetragonality (c/a ≈ 1.211), when forming a solid solution with SrTiO₃, it does not introduce tetragonal distortion, but instead leads to the appearance of non - perovskite phases at higher concentrations.