Reduced graphene oxide thin films as ultrabarriers for organic electronics

Hisato Yamaguchi,Jimmy Granstrom,Wanyi Nie,Hossein Sojoudi,Takeshi Fujita,Damien Voiry,Mingwei Chen,Gautam Gupta,Aditya D. Mohite,Samuel Graham,Manish Chhowalla

DOI: https://doi.org/10.1002/aenm.201300986

2013-10-15

Abstract:Encapsulation of electronic devices based on organic materials that are prone to degradation even under normal atmospheric conditions with hermetic barriers is crucial for increasing their lifetime. A challenge is to develop 'ultrabarriers' that are impermeable, flexible, and preferably transparent. Another important requirement is that they must be compatible with organic electronics fabrication schemes (i.e. must be solution processable, deposited at room temperature and be chemically inert). Here, we report lifetime increase of 1,300 hours for poly(3-hexylthiophene) (P3HT) films encapsulated by uniform and continuous thin (~10 nm) films of reduced graphene oxide (rGO). This level of protection against oxygen and water vapor diffusion is substantially better than conventional polymeric barriers such as CytopTM, which degrades after only 350 hours despite being 400 nm thick. Analysis using atomic force microscopy, x-ray photoelectron spectroscopy and high resolution transmission electron microscopy suggest that the superior oxygen gas/moisture barrier property of rGO is due to the close interlayer distance packing and absence of pinholes within the impermeable sheets. These material properties can be correlated to the enhanced lag time of 500 hours. Our results provide new insight for the design of high performance and solution processable transparent 'ultrabarriers' for a wide range of encapsulation applications.

Materials Science

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to develop an efficient, flexible and transparent "ultrabarrier" for encapsulating organic electronic devices, so as to significantly improve their service life under normal atmospheric conditions. Specifically, the research aims to overcome the defects existing in existing barrier materials (such as polymers and inorganic materials), such as inevitable pinholes, thickness limitations and complex preparation processes.

### Research Background and Problems

1. **Encapsulation Requirements for Organic Electronic Devices**:
- Organic materials are prone to degradation under normal atmospheric conditions, so efficient barrier materials are required to extend their lifespan.
- An ideal barrier should have the following characteristics: impermeable, flexible, transparent, and be compatible with the manufacturing processes of organic electronic devices (i.e., solution - processable, room - temperature deposition, chemically inert).

2. **Limitations of Existing Barrier Materials**:
- **Polymer Barriers** (such as Cytop™) have relatively high gas barrier performance, but usually require a relatively thick film layer (such as 400 nm) and are prone to pinholes.
- **Inorganic Barriers** (such as AlOx and SiOx) are prone to generate pinholes during the vacuum deposition process, and increasing the thickness will introduce stress cracks, resulting in new defects.
- **Multilayer Structures** (such as the "dyad" structure with alternating organic - inorganic stacking) can increase the length of the gas diffusion path, but increase the manufacturing complexity and reduce the flexibility.

### Research Objectives

The objective of this research is to achieve an efficient, flexible and transparent ultrabarrier by using reduced graphene oxide (rGO) films as barrier materials. Specific objectives include:

1. **Improve Barrier Performance**: Significantly improve the oxygen and water vapor barrier performance of rGO films by optimizing their preparation processes, especially through annealing treatment.
2. **Verify Barrier Effect**: Verify the protection effect of rGO films on organic materials (such as P3HT) through experiments, especially in the photo - oxidative degradation test.
3. **Explore Mechanisms**: Analyze the microstructure and physical properties of rGO films to reveal the internal mechanisms of their excellent barrier performance, especially the roles of long diffusion paths and tight layer spacing.
4. **Application Verification**: Apply the rGO barrier to actual organic electronic devices (such as BHJ organic solar cells) to verify its effectiveness in real - working environments.

### Conclusions

The research shows that a 10 - nm - thick rGO film prepared by the solution method can significantly improve the lifespan of organic materials to more than 1,300 hours, which is far superior to traditional polymer barriers (such as 400 - nm - thick Cytop™). In addition, the rGO film also has a high optical transmittance (75%) and good flexibility, making it an ideal candidate material for the future encapsulation of organic electronic devices.