Empirical relationship between x-ray photoemission spectra and electrical conductivity in a colossal magnetoresistive manganite La_{1-x}Sr_{x}MnO_{3}

T. Hishida,K. Ohbayashi,M. Kobata,E. Ikenaga,T. Sugiyama,K. Kobayashi,M. Okawa,T. Saitoh

DOI: https://doi.org/10.1063/1.4811372

2013-06-23

Abstract:By using laboratory x-ray photoemission spectroscopy (XPS) and hard x-ray photoemission spectroscopy (HX-PES) at a synchrotron facility, we report an empirical semi-quantitative relationship between the valence/core-level x-ray photoemission spectral weight and electrical conductivity in La_{1-x}Sr_{x}MnO_{3} as a function of x. In the Mn 2p_{3/2} HX-PES spectra, we observed the shoulder structure due to the Mn^{3+} well-screened state. However, the intensity at x=0.8 was too small to explain its higher electrical conductivity than x=0.0, which confirms our recent analysis on the Mn 2p_{3/2} XPS spectra. The near-Fermi level XPS spectral weight was found to be a measure of the variation of electrical conductivity with x in spite of a far lower energy resolution compared with the energy scale of the quasiparticle (coherent) peak because of the concurrent change of the coherent and incoherent spectral weight.

Strongly Correlated Electrons,Materials Science

What problem does this paper attempt to address?

This paper aims to explore the empirical relationship between X - ray photoelectron spectroscopy (XPS) and electrical conductivity in lanthanum - strontium manganite oxide (La\(_{1 - x}\)Sr\(_x\)MnO\(_3\), abbreviated as LSMO). Specifically, through laboratory XPS and hard X - ray photoelectron spectroscopy (HX - PES) techniques in synchrotron radiation facilities, the researchers analyzed the valence - band and core - level photoelectron spectra of LSMO samples with different strontium doping concentrations (x), and attempted to establish a quantitative relationship between these spectral features and the electrical conductivity of the material.

### Main problems
The main problems that the paper attempts to solve are:
1. **The relationship between the shoulder - peak structure in the Mn 2p3/2 level spectrum and electrical conductivity**: The researchers observed that there is a shoulder - peak structure in the HX - PES spectrum of the Mn 2p3/2 level, which is considered to be a well - shielded state of Mn\(^{3+}\) ions. However, when x = 0.8, although the electrical conductivity is high, the shoulder - peak intensity is very small, indicating that the metal behavior of the material cannot be explained solely by the shoulder - peak intensity.
2. **The relationship between the XPS spectral weight near the Fermi level and electrical conductivity**: The researchers found that the XPS spectral weight near the Fermi level (EF) can be used as a measure of the change in electrical conductivity, even though the energy resolution of XPS is much lower than the energy scale of the quasi - particle peak. This is because the change in the quasi - particle spectral weight and the spectral weight transfer of the incoherent part occur simultaneously.

### Key findings
- **The shoulder - peak structure in the Mn 2p3/2 level spectrum**: The shoulder - peak structure of the Mn 2p3/2 level was first observed in the sample with x = 0.8, confirming that this structure corresponds to the well - shielded state of Mn\(^{3+}\).
- **The relationship between electrical conductivity and spectral weight**: It was found that the XPS spectral weight near the Fermi level can well reflect the change in electrical conductivity, although the energy resolution of XPS is low. This indicates that the change in the quasi - particle spectral weight and the spectral weight transfer of the incoherent part occur simultaneously.
- **The contributions of Mn\(^{3+}\) and Mn\(^{4+}\)**: Electrical conductivity is determined not only by the spectral weight of Mn\(^{3+}\), but also by the spectral weight of Mn\(^{4+}\). The sum of the spectral weights of the two can better describe the change in electrical conductivity.

### Conclusion
Through XPS and HX - PES techniques, the researchers successfully established the relationship between the valence - band and core - level photoelectron spectral features and electrical conductivity in LSMO. In particular, the XPS spectral weight near the Fermi level can be used as a reliable indicator of the change in electrical conductivity, which is of great significance for understanding the electronic structure and giant magnetoresistance effect of LSMO.