Abstract:A carbon nanotube (CNT) tip was fabricated at the apex of an etched tungsten wire by chemical vapor deposition and used for scanning tunneling microscopy. The honeycomb lattice of graphite in the STM images was resolved with a CNT tip at T=79 K. The superior spatial resolution originating from the p orbitals of a CNT is responsible for the image of the honeycomb lattice of graphite in the STM images. The CNT tips are useful to image samples whose lattice constants are small and to get orbital information in samples with orbital ordering due to their superior spatial resolution with the sharp p orbitals.
What problem does this paper attempt to address?
The main problem that this paper attempts to solve is: how to achieve high - resolution imaging of the honeycomb lattice structure of graphite in a scanning tunneling microscope (STM) by using carbon nanotube (CNT) tips.
### Specific Problems and Solutions
1. **Limitations of Traditional STM Tips**:
- Traditional metal STM tips can usually only resolve the triangular lattice in graphite during imaging, and cannot directly observe the honeycomb - like lattice. This is because STM images are affected by electronic effects, causing the STM to resolve only one of the two carbon atom sites.
- The reason for this phenomenon is that the two carbon sites (α and β) in graphite have different electronic structures, causing the STM to selectively image different sites at different bias voltages.
2. **Advantages of CNT Tips**:
- The paper proposes using carbon nanotubes (CNT) as STM tips, taking advantage of their unique orbital structure (i.e., sharp p - orbitals) to improve spatial resolution.
- The high elasticity of CNT tips makes them less likely to be damaged by slight collisions and can provide higher spatial resolution, thus being able to resolve the honeycomb - like lattice of graphite.
3. **Experimental Results**:
- Using CNT tips for STM imaging at a low temperature of 79 K, the honeycomb - like lattice of graphite was successfully resolved.
- The experiment also showed selective imaging at different bias voltages, verifying the stability and resolution of CNT tips under different conditions.
4. **Explanation and Discussion**:
- The researchers excluded the influence of mechanical effects (such as double - tip effects, sample slippage, etc.) on the imaging results, and believed that the high resolution of CNT tips was due to their sharp p - orbitals and nanoscale size.
- The initial imaging results showed a triangular lattice, which may be due to contamination introduced during the SEM process. Long - time scanning helps to clean the CNT tips, thereby obtaining clearer honeycomb - like lattice images.
### Conclusion
This research has proven the superior performance of CNT tips in STM, especially in high - resolution imaging. This provides a new tool for studying materials with small lattice constants, for example, the d - orbital shape in CMR materials can be directly imaged. In addition, the application of CNT tips can also be extended to the field of multi - probe STM for nano - scale transport measurements.
### Examples of Mathematical Formulas
To better understand the STM imaging principle, the following formulas can be referred to:
- The relationship between the STM current \(I\) and the tunneling barrier height \(V\) can be expressed by the following formula:
\[
I = I_0 e^{-\beta (V - V_0)}
\]
where \(I_0\) is the initial value of the tunneling current, \(\beta\) is the tunneling attenuation coefficient, and \(V_0\) is the starting voltage.
- For the two carbon sites (α and β) in graphite, their electronic density of states \(D(\epsilon)\) can be expressed by the following formula:
\[
D_{\alpha}(\epsilon)\neq D_{\beta}(\epsilon)
\]
This difference causes the STM to selectively image different sites at different bias voltages.
Through these improvements, the researchers successfully achieved high - resolution imaging of the graphite honeycomb - like lattice.