Massive production of graphene oxide from expanded graphite

Ling Sun,Bunshi Fugetsu

DOI: https://doi.org/10.1016/j.matlet.2013.07.072

2013-01-15

Abstract:In a deviation from the conventional Hummers method, a spontaneous expansion approach was introduced with expanded graphite as the precursors. The intercalating agent (H2SO4) was able to penetrate into the expanded graphite; this had further expanded the graphite and as a result, a foam-like intermediate was produced. The foam-like graphite was more easily oxidized in reaction with the oxidant (KMnO4) to form graphene oxide (GO). Fully exfoliated GO was obtained with expanded graphite having the median diameter ~ 15 {\mu}m as the precursors. This procedure was much safer and productive in scalable applications than the conventional Hummers methods.

Materials Science

What problem does this paper attempt to address?

The problem this paper attempts to address is the safety and efficiency issues in the large-scale production of graphene oxide (GO) using existing methods. Although the traditional Hummers method is widely used, it has safety hazards and low yield issues, especially when dealing with larger graphite crystals, which can trigger rapid exothermic reactions, producing a large amount of purple smoke, leading to oxidant loss and reduced conversion efficiency. Additionally, the traditional method is complex to operate, requiring precise control of temperature and time, increasing the difficulty of industrial applications.

To solve these problems, the authors propose a new spontaneous expansion method, using commercial expanded graphite as a precursor. By introducing a spontaneous expansion step, the operation process is simplified, safety is improved, and yield is increased, making large-scale production of graphene oxide possible. Specifically, the method includes the following key steps:

1. **Precursor Selection**: Using commercial expanded graphite with a medium particle size (D50 ~ 15 μm).
2. **Spontaneous Expansion**: Further expanding the expanded graphite through the insertion of sulfuric acid to form a foam-like intermediate.
3. **Oxidation Reaction**: At room temperature, the foam-like intermediate reacts with potassium permanganate to produce graphene oxide.
4. **High-Temperature Hydrolysis**: Conducting high-temperature hydrolysis in a 90℃ water bath to finally obtain a uniform graphene oxide suspension.

This method not only simplifies the operation steps and improves safety but also significantly increases the yield, making it suitable for industrial large-scale production.