Effect of hollow glass microsphere on combustion behavior and mechanical properties of polyurethane foam

Shi Zhi-zhan

Abstract:Three-phase polyurethane foam was prepared by doping hollow glass microspheres into the foam of polyurethane.The oxygen index,horizontal burning rate and strain-stress parameters of three-phase polyurethane foam were investigated.The effects of the amount of hollow glass microspheres,dosage of ammonium polyphosphate(APP) and concentration of intumescent flame retardant(IFR) on the combustion behavior and mechanical properties of the three-phase polyurethane foam were studied.Results showed that doping hollow glass microsphere led to slight variation in the oxygen index and horizontal burning rate of as-prepared polyurethane foam.The introduction of APP or IFR helped to significantly improve the flame-retarding performance of the as-prepared polyurethane foam,and IFR was superior to APP in improving the flame-retarding performance of the foam.The oxygen index of the polyurethane foam rose to 24.9(higher than that of the undoped foam by 36.8%) and its horizontal burning rate declined to 302.6 mm/min(lower than that of undoped foam by 38.8%) when hollow glass microspere and IFR were simultaneously added at a mass fraction of 20%.In the meantime,doping hollow glass microspere led to changes in the stress-strain process of as-prepared polyurethane foam.Below the critical value of pressure,the strain of the three-phase foam slowly rose with increasing pressure.Above the critical value of pressure,however,the strain rose sharply with increasing pressure.

Engineering,Materials Science