Microwave dielectric properties of (1−x)ZnMoO4–xTiO2 composite ceramics
Jing Guo,Di Zhou,Hong Wang,Xi Yao
DOI: https://doi.org/10.1016/j.jallcom.2011.02.155
IF: 6.2
2011-01-01
Journal of Alloys and Compounds
Abstract:Highlights ► A new microwave dielectric system (1 − x )ZnMoO 4 – x TiO 2 was investigated. ► Triclinic wolframite ZnMoO 4 phase can coexist with tetragonal rutile TiO 2 phase. ► All the specimens can be well densified below 950 °C. ► The 0.842ZnMoO 4 –0.158TiO 2 composite ceramics with near-zero τ f value possesses a high Q × f value. ► Silver reacts with ZnMoO 4 easily and seems not to react with TiO 2 . Abstract (1 − x )ZnMoO 4 – x TiO 2 ( x = 0.0, 0.05, 0.158, 0.25, and 0.35) composite ceramics were synthesized by the conventional solid state reaction process. The sintering behavior, phase composition, chemical compatibility with silver, and microwave dielectric properties were investigated. All the specimens can be well densified below 950 °C. From the X-ray diffraction analysis, it indicates that the triclinic wolframite ZnMoO 4 phase coexists with the tetragonal rutile TiO 2 phase, and it is easy for silver to react with ZnMoO 4 to form Ag 2 Zn 2 (MoO 4 ) 3 phase and hard to react with TiO 2 . When the volume fraction of TiO 2 ( x value) increasing from 0 to 0.35, the microwave dielectric permittivity of the (1 − x )ZnMoO 4 – x TiO 2 composite ceramics increases from 8.0 to 25.2, the Q f value changes in the range of 32,300–43,300 GHz, and the temperature coefficient τ f value varies from −128.9 to 157.4 ppm/°C. At x = 0.158, the mixture exhibits good microwave dielectric properties with a ɛ r = 13.9, a Q f = 40,400 GHz, and a τ f = +2.0 ppm/°C. Keywords Microwave dielectric properties Composite LTCC ZnMoO 4 –TiO 2 1 Introduction With the explosive growth of high frequency wireless communication technology, electronic components and substrates are in urgent need of improving performances and realizing miniaturization and integration. It is possible to integrate the passive components to a function module by low temperature cofired ceramic (LTCC) technology. Materials with low sintering temperature (<960 °C), high quality factor ( Q f ) value and near zero temperature coefficient of resonant frequency ( τ f ) are necessary for the applications [1–4] . Recently, a number of new microwave dielectric ceramics have been developed, such as AWO 4 and AMoO 4 (A = Mg, Mn, Zn, Ca, Sr, and Ba). AWO 4 compounds have good dielectric properties: permittivity is 8–17, Q f value is 32,000–69,000 GHz, and τ f value is −53 to −78 ppm/°C [5] . AMoO 4 compounds are also suitable for applications of microwave dielectric materials, with low permittivity (7–11), low dielectric loss (37,000–90,000 GHz) and relatively small temperature coefficient of resonant frequency (−57 to −87 ppm/°C) [6] . Compared with AWO 4 , AMoO 4 ceramics have lower sintering temperature, especially ZnMoO 4 . However, all of them have negative τ f values. Normally, there are two methods to design a material with a stable temperature coefficient: (a) composite materials by mixing two or more component materials with opposite τ f values, including ZnAl 2 O 4 –TiO 2 , Ca 2 P 2 O 7 –TiO 2 , CaWO 4 –TiO 2 , Zn 2 Te 3 O 8 –TiO 2 , Zn 2 TiO 4 –TiO 2 , NiNb 2 O 6 –TiO 2 , and Bi 2 MoO 6 –TiO 2 [7–13] ; (b) formation of solid solutions, such as complex perovskites and other systems [14–17] . In the recent investigation, ZnMoO 4 sintered at 800 °C presents excellent microwave dielectric properties with ɛ r = 8.67 (permittivity), Q f = 49,900 GHz, τ f = −87.49 ppm/°C [6] . In order to compensate the negative τ f value of ZnMoO 4 , rutile TiO 2 ( ɛ r = 105, Q f = 46,000 GHz, τ f = +465 ppm/°C) [18] was selected to form a (1 − x )ZnMoO 4 – x TiO 2 mixture. In this work, the synthesis, sintering behavior, phase composition, chemical compatibility with silver, and microwave dielectric properties of the (1 − x )ZnMoO 4 – x TiO 2 mixture ceramics were studied. 2 Experimental All the samples were prepared by the conventional solid state reaction process. ZnO (>99%, Sinopharm Chemical Reagent Co., Ltd., China), MoO 3 (>99%, Fuchen Chemical Reagents, Tianjin, China) and rutile TiO 2 (>99%, Linghua Co., Ltd., Zhaoqing, China) were used as starting materials. The ZnMoO 4 powders were synthesized by calcining in air at 600 °C for 4 h. The ZnMoO 4 and TiO 2 powders were mixed according to the following stoichiometrics: (1 − x )ZnMoO 4 – x TiO 2 ( x = 0.0, 0.05, 0.158, 0.25 and 0.35; ZM, ZMT1, ZMT2, ZMT3, ZMT4 were used for abbreviations). The mixed powders were milled with ethanol and Zirconia milling media (2 mm in diameter) for 4 h using a planet ball-milling system whose running speed is 150 rpm, and then dried. The final powders mixed with PVA binder were pressed into cylinder samples (10 mm in diameter and 4–5 mm in height) and these pellets were sintered in the temperature range from 750 °C to 975 °C for 2 h with a heating rate of 3 °C/min. The phase compositions of the specimens were identified using X-ray diffraction with Cu Kα radiation (Rigaku D/MAX-2400 X-ray diffractometry, Tokyo, Japan). The microstructure was observed with a scanning electron microscope (JSM-6460, JEOL, Tokyo, Japan). The bulk densities of the specimens were measured by Archimedes’ method. The microwave dielectric properties were measured using the TE 01δ method with a network analyzer (8720ES, Agilent, Palo Alto, CA) and a temperature chamber (Delta 9023, Delta Design, Poway, CA). The temperature coefficient of resonant frequency ( τ f ) can be obtained by the following equation: (1) τ f = f 85 − f 25 f 25 ( 85 − 25 ) × 10 6 ( ppm/ ° C ) where f 85 and f 25 were the resonant frequencies at 85 °C and 25 °C, respectively. 3 Results and discussions Fig. 1 (a) shows the X-ray diffraction patterns of calcined ZnMoO 4 powders, ZnMoO 4 –TiO 2 composites cofired with 20 wt% Ag and Fig. 1 (b) shows the XRD patterns of (1 − x )ZnMoO 4 – x TiO 2 mixed phases sintered at 950 °C. The ZnMoO 4 with triclinic wolframite structure was obtained when calcined at 600 °C for 4 h. From Fig. 1 (b), it can be concluded that TiO 2 coexists with ZnMoO 4 . When the content of TiO 2 increasing, the intensity of the reflections of TiO 2 increases greatly. Finally, a study of the chemical compatibility of ZnMoO 4 –TiO 2 compounds with Ag powders has been made. As shown in Fig. 1 (a), Ag can form the Ag 2 Zn 2 (MoO 4 ) 3 phase with ZnMoO 4 easily, and seems not to react with TiO 2 . Fig. 2 presents the backscattered electron image of the surface of 0.65ZnMoO 4 –0.35TiO 2 sample. From the micrograph, it is seen that there are two types of grains in the specimen and the grain size is in the range of 1–6 μm. The EDS analysis shows that the light grains as B belong to ZnMoO 4 phase and the dark ones as A belong to the TiO 2 phase. Since the sintering temperature of pure TiO 2 ceramic is about 1300 °C [10] , the TiO 2 grains in the compounds are smaller than those of pure TiO 2 phase. Fig. 3 (a) presents the densities of the (1 − x )ZnMoO 4 – x TiO 2 ceramics. It can be seen that the densities of all the samples are larger than 4.06 g/cm 3 , which indicates that all the specimens’ relative densities are over 94%. Therefore, all the composite ceramics are well densified below 950 °C. The microwave dielectric properties of the (1 − x )ZnMoO 4 – x TiO 2 ceramics are shown in Fig. 3 (b) and (c). In the composite, the permittivity is determined by the permittivity, volume fraction and the complex form of the composing material [19] . If the composite material is aligned parallel to the electric field, the ɛ is given as [19] (2) ε = y 1 ε 1 + y 2 ε 2 where ɛ 1 and ɛ 2 are permittivities of material 1 and material 2, respectively; y 1 and y 2 are the volume fractions. When the composite material is aligned in series with the electric field, the ɛ can be obtained as follows [19] (3) 1 ε = y 1 ε 1 + y 2 ε 2 In case the composite material is aligned randomly, the ɛ follows the empirical logarithmic rule [19] (4) log ε = y 1 log ε 1 + y 2 log ε 2 In the (1 − x )ZnMoO 4 – x TiO 2 ceramics, the triclinic wolframite ZnMoO 4 phase and tetragonal rutile TiO 2 phase are distributed randomly. So the theoretical permittivity of the mixed ceramic can be gained by logarithmic rule. Fig. 3 (b) shows that the permittivity of the composite ceramic increases from 8.0 to 25.2 when the volume fraction of TiO 2 increasing from 0 to 0.35. Although the measured permittivity is a little higher than the theoretical value, it generally accords to the logarithmic rule. According to the empirical logarithmic rule, the τ f of the mixed ceramic can be obtained as follows: [13] (5) τ f = y 1 τ f 1 + y 2 τ f 2 where τ f 1 and τ f 2 are the τ f values of material 1 and material 2, respectively. The theoretical and measured τ f values are plotted in Fig. 3 (c). The measured τ f value shifts from −128.9 to 157.4 ppm/°C as x value increasing from 0 to 0.35. Compared with the previous reports [6,18] , the measured τ f value of pure ZnMoO 4 is a little lower and the measured τ f value of rutile TiO 2 is a little larger, which may be caused by the different calcination temperatures. The τ f values of (1 − x )ZnMoO 4 – x TiO 2 ceramics agree well with the mixture function (5) and the near-zero τ f value is obtained at x = 0.158. The permittivities and Q f values of the composite ceramics as a function of sintering temperature are plotted in Fig. 4 . It is seen that the (1 − x )ZnMoO 4 – x TiO 2 ceramics have good Q f values at low temperatures. The 0.35ZnMoO 4 –0.65TiO 2 composite has a minimum Q f value (32,300 GHz) and 0.05ZnMoO 4 –0.95TiO 2 composite has a maximum Q f value (43,300 GHz). The 0.842ZnMoO 4 –0.158TiO 2 composite with a near-zero τ f possesses a Q f value about 40,400 GHz. 4 Conclusion This study introduced a new dielectric material system (1 − x )ZnMoO 4 – x TiO 2 with good microwave dielectric properties. All the samples can be well densified below 950 °C. The X-ray analysis reveals that the triclinic wolframite ZnMoO 4 phase can coexist with the tetragonal rutile TiO 2 phase. Silver reacts with ZnMoO 4 easily to form the Ag 2 Zn 2 (MoO 4 ) 3 phase, and seems not to react with TiO 2 . When the volume fraction of TiO 2 was 0.158, the ɛ r , Q f value, and τ f value of the compound were 13.9, 40,400 GHz, and +2.0 ppm/°C, respectively. Acknowledgements This work was supported by the National 973-project of China ( 2009CB623302 ), NSFC projects of China ( 61025002 and 109790365 ) and National Project of International Science and Technology Collaboration ( 2009DFA51820 ). References [1] M.T. Sebastian H. Jantunen Int. Mater. Rev. 53 2008 57 90 [2] M. Valant D. Suvorov J. Am. Ceram. Soc. 83 2000 2721 2729 [3] A.K. Axelsson N.M. Alford J. Eur. Ceram. Soc. 26 2006 1933 1936 [4] D. Zhou H. Wang L.X. Pang C.A. Randall X. Yao J. Am. Ceram. Soc. 92 2009 2242 2246 [5] S.H. Yoon D.W. Kim S.Y. Cho K.S. Hong J. Eur. Ceram. Soc. 26 2006 2051 2054 [6] G.K. Choi J.R. Kim S.H. Yoon K.S. Hong J. Eur. Ceram. Soc. 27 2007 3063 3067 [7] K.P. Surendran N. Santha P. Mohanan M.T. Sebastian Eur. Phys. J. B 41 2004 301 306 [8] I.S. Cho S.K. Kang D.W. Kim K.S. Hong J. Eur. Ceram. Soc. 26 2006 2007 2010 [9] S.H. Yoon G.K. Choi D.W. Kim S.Y. Cho K.S. Hong J. Eur. Ceram. Soc. 27 2007 3087 3091 [10] G. Subodh M.T. Sebastian J. Am. Ceram. Soc. 90 2007 2266 2268 [11] C.F. Shih W.M. Li M.M. Lin C.Y. Hsiao K.T. Hung J. Alloys Compd. 485 2009 408 412 [12] Y.C. Liou Y.T. Chen W.C. Tsai J. Alloys Compd. 477 2009 537 542 [13] L.X. Pang H. Wang D. Zhou X. Yao J. Alloys Compd. 493 2010 626 629 [14] W.S. Kim K.H. Yoon E.S. Kim J. Am. Ceram. Soc. 83 2000 2327 2329 [15] J. Pei Z.X. Yue F. Zhao Z.L. Gui L.T. Li J. Alloys Compd. 459 2008 390 394 [16] S. Hirano T. Hayashi A. Hattori J. Am. Ceram. Soc. 74 1991 1320 1324 [17] D. Zhou C.A. Randall H. Wang L.X. Pang X. Yao J. Am. Ceram. Soc. 92 2009 2931 2936 [18] K. Fukuda R. Kitoh I. Awai Jpn. J. Appl. Phys. 32 1993 4584 4588 [19] Y. Imanaka Multilayered Low Temperature Cofired Ceramics (LTCC) Technology 2005 Springer New York