Spectral Investigation of Enhanced Orange Emission in Eu3+ Activated LaPO4 Nanophosphors Through Codoping With Na+ and Bi3+ Ions

Chandran Aswathy R,Jacob Linju Ann,Paul Issac,Jose Gijo,Mathew Prijil,Sisira S

DOI: https://doi.org/10.1002/bio.70010

IF: 2.613

2024-11-07

Luminescence

Abstract:The enhancement of luminescence intensity for orange emission in Eu3+ activated LaPO4 codoped with Na+ and Bi3+ is attributed to the improved crystallinity of the material. This optimized sample demonstrates significant potential as an orange‐emitting phosphor for applications in phosphor‐converted LEDs, as well as for use in forensic and high‐security applications. Lanthanum phosphate is a well‐known potential host for rare earth activators for phosphor‐converted white LED application. Na+ and Bi3+ codoped Eu3+ activated LaPO4 nanophosphor is successfully synthesized using citrate‐based hydrothermal method at ambient condition and confirmed by XRD, EDS and XPS analysis. The excitation spectra of the sample exhibit sharp f‐f characteristics peak of Eu3+ at 393 nm that is found to be the most dominant. The comparative photoluminescence studies of La1‐xPO4:xEu3+(x = 0.10), La1‐x‐y PO4:xEu3+, yNa+(x = 0.10, y = 0.05), and La1‐x‐y‐zPO4:xEu3+, yNa+, zBi3+ (x = 0.10, y = z = 0.05) reveal a progressive enhancement of the orange emission from Eu3+ as Na+ and (Na+, Bi3+) ions are incorporated into the LaPO4 matrix. The dominance of 5D0‐7F1 magnetic dipole transition contributing a major part of orange luminescence of the nanophosphors and the symmetric site occupancy of Eu3+ was justified from the observed trend of Ω4>Ω2 in the Judd–Ofelt intensity parameters. The CIE studies confirm the improvement in color purity of emission from 32.5% to 90.6% due to the presence of Na+ and Bi3+ions.

chemistry, analytical