Boosting the Initial Coulombic Efficiency of Sustainable Hard Carbon Derived from Polyethylene Terephthalate with Cyclopentyl Methyl Ether As a Co-Solvent for Wide-Temperature Sodium-Ion Batteries
Nagmani .,Dhrubajyoti Das,Sreeraj Puravankara
DOI: https://doi.org/10.1149/ma2023-021123mtgabs
2023-12-22
ECS Meeting Abstracts
Abstract:Upcycling plastic waste into value-added products helps to generate cost-effective and sustainable resources towards a circular materials economy and safer ecosystem. The conversion of polyethylene terephthalate (PET) municipal waste via the carbonization process into hard carbon (HC) delivers a high-reversible capacity, low-cost, sustainable anode material for sodium-ion batteries (SIBs). However, the low initial Coulombic efficiency (ICE) is a significant challenge of the HC anode, which should be optimized by electrolyte and interfacial chemistry. 1 In conventional carbonate esters-based electrolytes, ethylene carbonate (EC) forms an organic-rich thick SEI layer, soluble on cycling, limiting the cyclic stability. The low-temperature performance is also a significant concern in achieving high capacity, long cyclability, and ICE. 2 Herein, HC derived via single-step carbonization at 1000°C exhibits larger interlayer spacing of 0.379 nm, low surface area (~205 m 2 g -1 ), and unique slit-shaped pores with 84% mesoporosity in the structure. PET-HC exhibits a high reversible capacity of 337 mAh g -1 with ICE of just 66%, using EC-PC-based electrolyte. EC-free cyclopentyl methyl ether (CPME) was used due to its weakly solvating and wide temperature solvent. 3 CPME-PC-based electrolytes significantly enhanced the ICE value to 74.5% and reversible capacity to 356 mAh g -1 with superior cycling of 91% after 100 cycles at 0.1C rate. The inorganic-rich SEI layer for CPME-PC-based electrolytes results in a thin SEI that improves the ICE and cyclic stability of the anode. The low-temperature performance (up to -20°C) for CPME-PC-based electrolytes showed ~30% added capacity compared to EC-PC-based electrolytes. This work provided an eco-friendly approach to developing hard carbons from plastic trash and offered an effective strategy to replace EC with CPME for low-temperature sodium storage applications. References Shen, L., Shi, S., Roy, S., Yin, X., Liu, W., Zhao, Y., Adv. Funct. Mater. 2021 , 31 , 2006066. Ramasamy, H. V., Kim, S., Adams, E. J., Rao, H. & Pol, V. G. Chem. Commun. 2022 , 58 , 5124–5127. Zhang, H., Zeng, Z., Ma, F., Wu, Q., Wang, X., Cheng, S., Xie, J., Angew. Chem. 2023 , e202300771. Figure 1