Facile synthesis and step by step enhancement of blue photoluminescence from Ag-doped ZnS quantum dots

Sonal Sahai,Mushahid Husain,Virendra Shanker,Nahar Singh,D. Haranath

DOI: https://doi.org/10.1016/j.jcis.2011.02.030

2012-11-16

Abstract:Our results pertaining to the step by step enhancement of photoluminescence (PL) intensity from ZnS:Ag,Al quantum dots (QDs) are presented. Initially, these QDs were synthesized using a simple co-precipitation technique involving a surfactant, polyvinylpyrrolidone (PVP), in de-ionised water. It was observed that the blue PL originated from ZnS:Ag,Al QDs was considerably weak and not suitable for any practical display application. Upon UV (365 nm) photolysis, the PL intensity augmented to ~170% and attained a saturation value after ~100 minutes of exposure. This is attributed to the photo-corrosion mechanism exerted by high-flux UV light on ZnS:Ag,Al QDs. Auxiliary enhancement of PL intensity to 250% has been evidenced by subjecting the QDs to high temperatures (200oC) and pressures (~120 bars) in a sulphur-rich atmosphere, which is due to the improvement in crystallanity of ZnS QDs. The origin of the bright blue PL has been discussed. The results were supported by x-ray phase analysis, high-resolution electron microscopy and compositional evaluation.

Materials Science,Chemical Physics

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to increase the blue - light photoluminescence (PL) intensity of ZnS:Ag,Al quantum dots (QDs) so as to make them suitable for practical display applications. Specifically:

1. **Initial problem**: ZnS:Ag,Al quantum dots prepared by the co - precipitation method exhibit weak blue - light photoluminescence, which limits their application in practical display devices.
2. **Solutions**:
- **UV photolysis (UVP) treatment**: Through high - flux ultraviolet light (365 nm) irradiation, the PL intensity increased by approximately 170% and reached saturation after about 100 minutes. This enhancement is attributed to the photo - corrosion mechanism.
- **UV photolysis combined with polysulfide hydrothermal treatment (UVP + PSH)**: Further increased the PL intensity to 250%. This treatment method not only increased the PL intensity but also improved the crystallinity and morphology of the quantum dots.

### Specific steps and results

- **Co - precipitation synthesis**: ZnS:Ag,Al quantum dots were synthesized in deionized water using polyvinylpyrrolidone (PVP) as a surfactant.
- **UV photolysis (UVP)**: The sample was irradiated with a 125 - W ultraviolet lamp with a wavelength of 365 nm for about 180 minutes, and a significant increase in PL intensity was observed.
- **Polysulfide hydrothermal treatment (PSH)**: The UV - irradiated sample was treated in a polysulfide environment at high temperature and high pressure (200 °C, ~ 120 bar), further enhancing the PL intensity.

### Conclusion

Through the above treatment methods, especially the UVP + PSH treatment, a significant increase in the blue - light PL intensity of ZnS:Ag,Al quantum dots (up to 250%) was achieved. These improvements make the quantum dots have higher brightness and better structural properties, making them more suitable for application in high - resolution, high - brightness, and high - contrast display devices.

### Related formulas

- **Photo - corrosion reaction**:
\[
\text{ZnS}+2\text{H}_2\text{O}+\text{O}_2\rightarrow\text{Zn}^{2 +}+\text{SO}_4^{2 -}+4\text{H}^+
\]
- **Time - resolved photoluminescence (TRPL) decay equation**:
\[
\text{Decay}=A + B_1e^{-t/\tau_1}+B_2e^{-t/\tau_2}
\]
where \(\tau_1\) and \(\tau_2\) are decay constants, and \(A\), \(B_1\) and \(B_2\) are constants related to the equation. The two decay constants measured experimentally are 1.72 µs and 53.07 µs respectively.

Through these improvements, the PL performance of ZnS:Ag,Al quantum dots has been significantly improved, making them an ideal choice for blue - light components in nano - display systems.