Extended defects in natural diamonds: Atomic Force Microscopy investigation

Radmir V. Gainutdinov,Andrey A. Shiryaev,Yana Fedortchouk
DOI: https://doi.org/10.1016/j.diamond.2013.09.006
2012-09-07
Abstract:Surfaces of natural diamonds etched in high-pressure experiments in H2O, CO2 and H2O-NaCl fluids were investigated using Atomic Force Microscopy. Partial dissolution of the crystals produced several types of surface features including the well-known trigons and hillocks and revealed several new types of defects. Besides well-known trigons and dissolution hillocks several new types of defects are observed. The most remarkable ones are assigned to anelastic twins of several types. The observation of abundant microtwins, ordering of hillocks and presence of defects presumably related to knots of branched dislocations suggests importance of post-growth deformation events on formation of diamond microstructure. This work confirms previous reports of ordering of extended defects in some deformed diamonds. In addition, the current work shows that natural diamonds deform not only by dislocation mechanism and slip, but also but mechanical twinning. The dominant mechanism should depend on pressure-temperature-stress conditions during diamond transport from the formation domain to the Earth surface.
Materials Science,Geophysics
What problem does this paper attempt to address?
The main problem that this paper attempts to solve is to explore the changes in the surface characteristics of natural diamonds after dissolution in high - pressure experimental environments (such as in H₂O, CO₂ and H₂O - NaCl fluids), and to reveal the extended defects on and within their surfaces through Atomic Force Microscopy (AFM). Specifically, the research aims to: 1. **Identify new surface features**: Besides the known trigons and hillocks, the research has also discovered several new defect types. 2. **Understand the deformation mechanisms**: By observing microtwins, hillock arrangements and defects related to branching dislocation junctions, the influence of post - formation deformation events on the microstructure of natural diamonds is explored. 3. **Confirm the orderliness of extended defects**: Verify previous reports on the orderliness of extended defects in some deformed diamonds and further explore the causes of this orderliness. 4. **Reveal the deformation mechanisms**: Prove that natural diamonds are deformed not only through dislocation mechanisms and slip, but also through mechanical twinning, and that the main deformation mechanism depends on the pressure - temperature - stress conditions when the diamond is transported from the formation area to the surface. ### Specific problem analysis #### 1. **Identify new surface features** The paper studied in detail the dissolution characteristics of natural diamonds in different fluids through AFM and discovered new defect types, especially anelastic twins. The existence of these twins indicates that the diamond has undergone significant deformation events after formation. #### 2. **Understand the deformation mechanisms** The research found that the existence of microtwins, hillock arrangements and defects related to branching dislocation junctions implies that complex stress actions occurred during the post - formation deformation process of natural diamonds. These findings are helpful for understanding the deformation mechanisms of diamonds under geological conditions. #### 3. **Confirm the orderliness of extended defects** Through AFM and other analytical techniques (such as small - angle scattering and transmission electron microscopy), the research has confirmed the orderliness of extended defects in some deformed diamonds. This orderliness may be caused by the superposition of multiple stress fields, such as the stress fields from dislocations. #### 4. **Reveal the deformation mechanisms** The paper points out that natural diamonds are deformed not only through dislocation mechanisms and slip, but also through mechanical twinning. The main deformation mechanism depends on the pressure - temperature - stress conditions when the diamond is transported from the formation area to the surface. This provides a new perspective for understanding the deformation of diamonds in geological processes. ### Conclusion This research has revealed the complex defect structures on and within the surfaces of natural diamonds through AFM, especially the existence of microtwins, indicating that the diamond has undergone significant deformation events after formation. These findings are not only helpful for understanding the microstructure and deformation mechanisms of diamonds, but also provide an important reference for geology and gemology.