States of W in diamond-like carbon coatings and its effects on hybrid structure and mechanical performance: Molecular dynamics simulations

Jihua Peng,Jinhai Huang

DOI: https://doi.org/10.1016/j.mtcomm.2024.108206

IF: 3.8

2024-01-30

Materials Today Communications

Abstract:In this study, the bond-order potential based on the traditional Tersoff formula was selected to describe the interaction between atom pairs, and W-doped diamond-like carbon (W-DLC) films were simulated using the platform package of the large-scale atomic/molecular massively parallel simulator and OVITO interface software. We examined the effect of W dopant content on the states of W atoms in the films as well as their hybrid structure, hardness, and residual stress. The results indicate that W atoms preferentially combine with neighboring C atoms to form W–C bonds, which hinders the formation of metallic W clusters. The W carbide crystallites nucleated from the W–C clusters only when the W content was greater than 2 at%. Below this value, some isolated small W–C clusters were dispersed in the C matrix. As the W content increased, the tungsten carbide compound clusters grew until the films became WC-based films; both the sp 3 C and sp 2 C fractions in the films decreased monotonically, while the sp 3 C/sp 2 C ratio increased. Compared with the film without W, a lower residual stress and higher hardness can be achieved for W-DLC films with less than 6 at% W.

materials science, multidisciplinary