Abstract:NiOx thin films approximately 300 nm thick were deposited on indium tin oxide (ITO)-coated glass substrates by magnetron sputtering. Their electrochromic properties were tested in a 1 M potassium hydroxide (KOH) aqueous solution and in a 1 M lithium perchlorate dissolved in propylene carbonate (LiClO4-PC) anhydrous electrolyte, respectively. The evolution of the lattice structure, surface morphology, chemical composition, optical transmittance modulation, cyclic voltammograms, inserted and extracted charge capacities of NiOx thin films was evaluated as a function of the number of cycles. Even though the cyclic voltammograms and the charge capacity present a similar variation tendency during 1000 cycles, significant differences between cycling in 1 M KOH and 1 M LiClO4-PC were observed. In 1 M KOH, X-ray diffraction (XRD) results showed that the lattice planes (111) and (200) had a larger shift toward higher diffraction angles, and SEM images exhibited that cracks emerged more quickly from the surface of NiOx thin film during the cycling process. More importantly, the optical modulation varying from 58.5% to 32.9% presented an obvious degradation after 1000 cycles. On the contrary, in 1 M LiClO4-PC, NiOx thin films presented a better cyclic durability and a stable optical modulation approximating 41%. In a second step, an all-solid-state complementary electrochromic device with an ITO/WO3/LiClO4-PC-PMMA/NiOx/ITO structure was assembled. The device had an average optical modulation of 51.7% in the visible region and an excellent cyclic durability (over 50,000 times). In situ optical transmittance spectra showed that, in the initial cycles, the response time was 4.5 s for the coloring process and 1.7 s for the bleaching process. After 1000 cycles, both were delayed to 5.0 s and 2.9 s, respectively. In addition, open circuit memory of the device was characterized by the optical transmittance variation plotted against time after disconnection of the external circuit. (C) 2016 Elsevier B.V. All rights reserved.

Electro-optical performance of solid-state electrochromic device based on self-supporting electrolyte

Study of proton-based long-cycle-life all-solid-state electrochromic device

Transparent Succinonitrile-Modified Polyacrylate Gel Polymer Electrolyte for Solid Electrochromic Devices

All-solid-state electrochromic devices based on the LiAlSiO4 electrolyte

A Strong and Highly Transparent Ionogel Electrolyte Enabled by In Situ Polymerization-Induced Microphase Separation for High-Performance Electrochromic Devices

An all-solid-state electrochromic device based on NiO/WO3 complementary structure and solid hybrid polyelectrolyte

Electro-optical performance of all solid state electrochromic devices with NaF electrolytes

Inorganic Multi-Color Transmissive-Type Electrochromic Electrodes Based on Fabry-Perot Interferometer for Full-Solid Smart Window

Ultra-strong ionic liquid-based polymer composite electrolyte for high performance electrochromic devices

High-performance electrochromic WO3 film driven by controllable crystalline structure and its all-solid-state device

Electrochromic Devices Constructed with Water-in-Salt Electrolyte Enabling Energy-Saving and Prolonged Optical Memory Effect

Effect of independently controllable electrolyte ion content on the performance of all-solid-state electrochromic devices

Electro-optical performance of the quasi-solid-state electrochromic device with Mg 2+ electrolyte

Electrochromic performance and potential stability of sputtered V2O5 film for a complementary inorganic all-solid-state electrochromic device

Electrolytes-relevant cyclic durability of nickel oxide thin films as an ion-storage layer in an all-solid-state complementary electrochromic device

Enhanced Contrast of WO3-Based Smart Windows by Continuous Li-Ion Insertion and Metal Electroplating.

All Solid State Electrochromic Devices Based on the LiF Electrolyte.

Electro-optical Performance of the Quasi-Solid-state Electrochromic Device with Mg2+electrolyte

A large-area, flexible, high contrast and long-life stable solid-state electrochromic device driven by an anion-assisted method

High-performance of Quasi-Solid-state Complementary Electrochromic Devices Based on Al3+/Li+ Dual-Ion Electrolyte

Extraordinarily fast response all-solid-state electrochromic devices