Imidazolium ionic liquids as neat lubricant for electroplating Sn on Cu substrate under sliding electrical contact at high temperatures up to 80 °C

Yanan Qiao,Linpeng Chen,Feiyan Yuwen,Zhiqin Ding,Zujun Chen,Bo Wang,Wu Zhang,Jinjun Lu,Ruiqing Yao

DOI: https://doi.org/10.1016/j.apsusc.2023.158677

IF: 6.7

2023-10-16

Applied Surface Science

Abstract:Three kinds of imidazolium ionic liquids (IILs) with different fluorine-containing anions, i.e. imidazolium tetrafluoroborate (LB108), imidazolium hexafluorophosphate (LP108), imidazolium methyltributylammomiumbis ((trifluoromethyl)sulfonyl)imide ([HEMIM]NTf 2 ), are selected as neat lubricant for electroplating Sn on Cu substrate under sliding electrical contact at room temperature (25 °C) and elevated temperatures (40 °C and 80 °C). All the IILs effectively reduce friction coefficient (0.28 for LB108 and LP108, 0.4 for [HEMIM]NTf 2 ) and prevent Sn film from rapidly worn out and severe adhesive wear at 25 °C. However, at high temperatures, only LB108 well lubricate Sn-on-Sn contact up to 80 °C. It is found that, at 80 °C, the microstructure and chemical composition of the worn surface and the subsurface of the electroplating Sn are markedly modified due to two aspects: (1) temperature related phenomena (i.e. thermal diffusion of Cu to Sn film and even to SnO 2 layer, as well as formation of intermetallic phase Cu 6 Sn 5 ) and (2) interaction of the worn surface and IILs (i.e. adsorption, tribochemical interaction of the worn surface and the anion species, and diffusion of N species in Sn film). The interaction of the worn surface and the anion species of IILs plays an important role in wear reduction of electroplating Sn at 80 °C.

chemistry, physical,physics, applied, condensed matter,materials science, coatings & films