Co/Co 2 P Nanoparticles Encapsulated within Hierarchically Porous Nitrogen, Phosphorus, Sulfur Co‐doped Carbon as Bifunctional Electrocatalysts for Rechargeable Zinc‐Air Batteries
Likai Wang,Yinggang Sun,Shenzhi Zhang,Hexiang Di,Qiming Liu,Xin Du,Zhongfang Li,Kai Yang,Shaowei Chen
DOI: https://doi.org/10.1002/celc.202101246
IF: 4
2021-11-12
ChemElectroChem
Abstract:Developing high performance nonprecious metal‐based electrocatalysts has become a critical first step towards commercial applications of metal‐air batteries. Herein, nanocomposites based on Co/Co2P nanoparticles encapsulated within hierarchically porous N, P, S co‐doped carbon are prepared by controlled pyrolysis of zeolitic imidazolate frameworks (ZIF‐67) and poly(cyclotriphosphazene‐co‐4,4’‐sulfonyldiphenol) (PZS). The resulting Co/Co2P@NPSC nanocomposites exhibit apparent oxygen reduction reaction (ORR) and evolution reaction (OER) catalytic performance, and are used as the reversible oxygen catalyst for zinc‐air batteries (ZABs). Density functional theory (DFT) calculations exhibit that Co2P could provide active sites for the ORR and promote the conversion between the adsorbed intermediates, and porous N,P,S co‐doped carbon with Co2P nanoparticles also improves the exposure of actives sites and endows charge transport. Liquid‐state ZABs with Co/Co2P@NPSC as the cathode catalysts demonstrate the greater power density of 198.1 mW cm−2 and a long cycling life of 50 h at 10 mA cm−2, likely due to the encapsulation of Co/Co2P nanoparticles by the carbon shell. Solid‐state ZABs also display a remarkable performance with a high peak power density of 74.3 mW cm−2. Therefore, this study indicates the meaning of the design and engineering of hierarchical porous carbon nanomaterial as electrocatalyst for rechargeable metal‐air batteries. In a ZIF: A hybrid composite based on Co/Co2P nanoparticles encapsulated within N,P,S co‐doped porous carbon is prepared by controlled pyrolysis of a cobalt‐containing zeolitic imidazolate framework (ZIF‐67) and poly(cyclotriphosphazene‐co‐4,4’‐sulfonyldiphenol) (PZS). Electrochemical measurements show enhanced oxygen reduction reaction activity and long‐term durability compared with commercial Pt/C, whereas the oxygen evolution reaction activity and stability are comparable to that of RuO2. A rechargeable zinc‐air battery in liquid electrolyte is fabricated, which demonstrates a high peak power density of 198.1 mW cm−2, a specific capacity of 890.5 mAh−1Zn, low discharge and charge of polarization, and a long cycling life of 50 h at 10 mA cm−2.
electrochemistry