Abstract:High quality stoichiometric magnetite (Fe3O4) films grown by infrared pulsed laser deposition (IR-PLD) on different surfaces were investigated in order to study the influence of the substrate, orientation, and thickness on their magnetic behavior. Different single crystal (001)-oriented substrates, i.e., SrTiO3(001), MgAl2O4(001) and MgO(001), have been used for the preparation of epitaxial Fe3O4(001) films. By comparison, polycrystalline magnetite films were obtained on both single crystal Al2O3(0001) and amorphous Si/SiO2 substrates. The thickness has been varied between 50 - 400 nm. All films consist of nanocrystalline stoichiometric magnetite with very small strain (<1\%) and present the Verwey transition (Tv) between 110-120 K, i.e., close to bulk magnetite (122 K). In general, Tv depends on both microstructure and thickness, increasing mainly as the thickness increases. Room temperature angular-dependent measurements reveal an in-plane fourfold symmetry magnetic behavior for all films grown on (001)-oriented surfaces, and with the easy axes lying along the Fe3O4 [010] and [100] directions. Remarkably, the fourfold magnetic symmetry shows up to 400 nm thick films. In turn, the films grown on single crystal Al2O3 (0001) and on amorphous Si/SiO2 surfaces display an isotropic magnetic behavior. Coercive field (Hc) depends on microstructure and film thickness. The largest (lowest) Hc value corresponds to the thinner film grown on a single crystal SrTiO3(001) (amorphous Si/SiO2) surface, which present the largest (lowest) strain (crystallinity). Moreover, the coercivity follows an inverse law with film thickness. Our results demonstrate that we can artificially control the magnetic behavior of stoichiometric IR-PLD grown Fe3O4 films by exploiting substrate-induced anisotropy and thickness-controlled coercivity, that might be relevant to incorporate magnetite in future spintronic devices.

Magnetism in nanometer-thick magnetite

Nanomagnetism of magnetoelectric granular thin-film antiferromagnets

Fe3O4 thin films: controlling and manipulating an elusive quantum material

Ultrathin Ferrite Nanosheets for Room-Temperature Two-Dimensional Magnetic Semiconductors.

Magnetic and Electronic Properties of Anisotropic Magnetite Nanoparticles

van der Waals epitaxial growth and high-temperature ferrimagnetism in ultrathin crystalline magnetite (Fe 3 O 4 ) nanosheets

Enhanced magnetic moment and conductive behavior in NiFe2O4 spinel ultrathin films

Large Low Field Magnetoresistance In Ultrathin Nanocrystalline Magnetite Fe3o4 Films At Room Temperature

Towards magnetic control of magnetite

Short-Range Correlations in Magnetite above the Verwey Temperature

Nanometer thick magneto-optical iron garnet films

Enhanced Ferromagnetism in Atomically Thin Oxides Achieved by Interfacial Reconstruction

The role of faceting and elongation on the magnetic anisotropy of magnetite Fe3O4 nanocrystals

Micromagnetism in (001) magnetite by spin-polarized low-energy electron microscopy

Magnetization Switching of Single Magnetite Nanoparticles Monitored Optically

Magnetic properties and morphology of ultra-small iron oxide nanoparticles

Magnetic nanoparticles: from the nanostructure to the physical properties

Material Characterization Study of Magnetite Nanocrystals for RF Sensing

Antiferromagnetic Nanoscale Bit Arrays of Magnetoelectric Cr 2 O 3 Thin Films

Insight on thermal stability of magnetite magnetosomes: implications for the fossil record and biotechnology

Fingerprinting the magnetic behavior of antiferromagnetic nanostructures using remanent magnetization curves