Abstract:Hierarchical ZSM‐5 zeolite materials with different SiO2/Al2O3 molar ratios in the range of 60–300 were synthesized using soft templating and microemulsion methods to generate zeolite materials with narrow mesopore size distributions. The resulting materials were characterized by X‐ray flourescence (XRF), Fourier transform infra‐red (FTIR) spectroscopy, X‐ray diffraction (XRD), scanning electron microscopy (SEM), ammonia temperature programmed desorption (NH3‐TPD), thermo‐gravimetric analysis (TGA), Brunauer‐Emmett‐Teller (BET) surface area measurements, and products from the catalytic tests were analyzed by gas chromatography (GC). The XRF analysis determined that the Si/Al ratios for the synthesized ZSM‐5 were close to the batch ratios. The XRD and FTIR results revealed that the synthesized samples had crystalline ZSM‐5 zeolite structures. The small angle observed from the XRD patterns confirmed the presence of mesopores in the structure of the prepared materials. The SEM results showed that the ZSM‐5 synthesized materials had different morphologies and particle sizes, as well as worm‐like holes indicating that some macropores with average pore sizes ranging between 68 and 85 nm were successfully generated in these materials. NH3‐TPD results showed that the total acidity of the prepared materials decreased with an increase in the Si/Al (SA) ratio following this trend: SA = 71 > 177 > 345. This may be due to the decrease in the aluminum content, which is largely responsible for the formation of acidic sites in zeolites. The acid strength was found to increase with a decrease in the Si/Al ratio, highlighted by the peak shifts to higher temperatures. From the BET results, the SA = 71 was observed to have the highest SSA of 618 m2/g given by its micropore area of 103 m2/g and an external surface area of 515 m2/g. The high external surface area present in the material was due to the development of mesopores with narrow pore size distribution of approximately 6 nm indicating the success of the microemulsion method for the generation of hierarchical zeolites with well controlled pore sizes. The hierarchical ZSM‐5 catalysts were tested for the cracking of various hydrocarbon chain lengths. Low conversions, less than 10%, were obtained in the cracking of hexane; however, when cracking longer chain C12 hydrocarbons, the conversion increased remarkably to 100%. The catalyst with SA = 71 had the highest selectivity towards ethylene and propylene olefins due to its higher acidity in comparison with the other prepared catalysts. Improved activity, selectivity towards ethylene and propylene greater than 60%, and enhanced catalyst stability were demonstrated when using a hierarchical ZSM‐5 compared to the commercial catalyst in the cracking of dodecane. High selectivity towards light olefins was obtained for the cracking of waste tire‐derived oil. The results suggest that these hierarchical materials are suited to the cracking of long chain hydrocarbons and are promising materials for the valorization of waste tire‐derived oils.

Development of hierarchical ZSM-11 for synthesis of light olefins from crude oil

Effective hierarchical ZSM‐5 catalysts for the cracking of naphtha and waste tire‐derived oil to light olefins

Facile Synthesis of Nanosheet-Stacked Hierarchical ZSM-5 Zeolite for Efficient Catalytic Cracking of n-Octane to Produce Light Olefins

Synthesis and Assessment of Y-Zeolite Catalyst for Direct Olefin Production from Heavy Feedstock: An Effect of Feed Composition

Synthesis and Performance of Pillared HZSM-5 Nanosheet Zeolites for N-Decane Catalytic Cracking to Produce Light Olefins

Synthesis of Two-Dimensional Zeolite Nanosheets Applied to the Catalytic Cracking of a Waste Cooking Oil Model Compound to Produce Light Olefins

Effect of Hierarchical ZSM-5 Zeolite Crystal Size on Diffusion and Catalytic Performance of N-Heptane Cracking

Highly Selective Hierarchical ZnO/ZSM-5 Catalysts for Propane Aromatization

Catalytic Cracking of Crude Oil: Mini Review of Catalyst Formulations for Enhanced Selectivity to Light Olefins

ZSM–5@KIT–6 encapsulated composite molecular sieves for the catalytic cracking of waste cooking oil model compound to produce light olefins

Hierarchical Zeolites as Catalysts for Biodiesel Production from Waste Frying Oils to Overcome Mass Transfer Limitations

Tuning Hierarchical ZSM-5 Zeolite for Both Gas- and Liquid-Phase Biorefining

Facile synthesis of hierarchical macro/microporous ZSM-5 zeolite with high catalytic stability in methanol to olefins

Transition metal modified hierarchical ZSM-5 nanosheet for catalytic cracking of n -pentane to light olefins

Catalytic Cracking of n-Dodecane to Chemicals: Effect of Variable-Morphological ZSM-5 Zeolites Synthesized Using Various Silica Sources

Hierarchical ZSM-5 Supported CoMn Catalyst for the Production of Middle Distillate from Syngas

Synthesis of Nanoscale ZSM-5 Zeolites for the Catalytic Cracking of Oleic Acid into Light Olefins and Aromatics

Catalytic Performance of Methanol to Aromatics over Hierarchical ZSM-5 Zeolite Synthesized by a Soft Template Method

A novel anionic surfactant as template for the development of hierarchical ZSM-5 zeolite and its catalytic performance

ZSM-5 Catalysts for MTO: Effect and Optimization of the Tetrapropylammonium Hydroxide Concentration on Synthesis and Performance.