Ag–In–Zn–S Quantum Dot-Dominated Interface Kinetics in Ag–In–Zn–S/NiFe LDH Composites toward Efficient Photoassisted Electrocatalytic Water Splitting
Dongxu Zhang,Weixuan Dong,Yanhong Liu,Xiaoqing Gu,Tianyu Yang,Qiang Hong,Di Li,Dongqi Zhang,Hongbo Zhou,Hui Huang,Baodong Mao,Zhenhui Kang,Weidong Shi
DOI: https://doi.org/10.1021/acsami.1c09948
2021-08-25
Abstract:Photoassisted electrocatalysis (P-EC) emerges as a rising star for hydrogen production by embedding photoactive species in electrocatalysts, for which the interfacial structure design and charge transfer kinetics of the multifunctional catalysts remain a great challenge. Herein, Zn-AgIn5S8 quantum dots (ZAIS QDs) were embedded into 2D NiFe layered double hydroxide nanosheets through a simple hydrothermal treatment to form 0D/2D composite catalysts for P-EC. With evidence from transient photovoltage spectroscopy, we acquired a clear and fundamental understanding on the kinetics of charge extraction time and extraction amount in the 0D/2D heterojunctions that was proved to play a key role in P-EC. Upon light illumination, for HER, the optimized NiFe-ZAIS exhibits obviously reduced overpotentials of 129 and 242 mV at current densities of 10 and 50 mA cm–2, which are 22 and 33 mV lower than those of dark electrocatalysis, respectively. For OER, the NiFe-ZAIS electrode also shows low overpotentials of 220 and 268 mV at current densities of 10 and 50 mA cm–2, respectively, under light illumination, which were able to almost double the intrinsic activity. Finally, with as both the cathode and the anode, the assembled electrolyzer only requires 1.62 V to reach the overall water splitting current density of 10 mA cm–2 under P-EC. This work provides a useful example for the profound understanding of the design and the kinetics study of multifunctional P-EC catalysts.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.1c09948.Experimental section; XRD patterns, SEM and TEM images, PL, and UV–vis spectra of ZAIS QDs, NiFe LDH, and NiFe-ZAIS; XPS full spectra of ZAIS QDs, NiFe LDH, and NiFe-ZAIS; comparison of TPV relaxation curves of ZAIS QDs, NiFe LDH, and NiFe-ZAIS; equivalent circuit for fitting the resistance values of OER and HER; XPS patterns of NiFe-ZAIS before and after reaction; and the values of the resistance of the equivalent circuits for catalysts in OER and HER (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology