Abstract:An Al‐containing MIL‐53 metal‐organic framework with very high surface area (SBET=1130 m2.g−1, N2 sorption) was used as sacrificial template to prepare a nickel‐alumina‐based catalyst (Ni0AlMIL) highly active and stable in the reaction of dry reforming of methane (DRM). The procedure consisted in impregnating the activated (solvent free) MIL‐53 sample with a nickel precursor solution, then calcining the material to remove the organic linkers and subsequently reducing it to form the reduced nickel active phase. At the step of calcination, this procedure results in the formation of a porous uniform spinel phase with Ni nanospecies embedded in the alumina‐based matrix, as deduced from XRD, TPR and TEM analyses. This leads after reduction to a porous lamellar γ‐Al2O3 material with small Ni0 nanoparticles homogeneously dispersed and stabilized within the support. The performances of this catalyst in DRM are better than those of two reference Ni/alumina catalysts prepared for comparison by conventional nickel impregnation of two preformed alumina supports: a first one obtained by calcination of MIL‐53 (AlMIL) and a second one consisting of a commercial γ‐Al2O3 batch (AlCOM). Under steady state conditions at a temperature of 650 °C and a pressure of 1 bar, the higher CH4 and CO2 conversions (till 3 times higher than on Ni0/AlCOM), high catalytic stability (no loss of activity after 13–100 h) and higher selectivity towards DRM (H2:CO products ratio remaining at 1) on Ni0AlMIL compared to the other catalysts is believed to come from the particularly strong interaction between the nickel and alumina phases generated by using the unique high specific surface of the parent MOF support to deposit nickel. This creates an intimate mixing favorable to a persisting interaction of the nickel nanoparticles with the alumina support in the reduced material. The lamellar shape of the γ‐Al2O3 composing the catalyst and its remaining high specific surface may also contribute to the excellent Ni resistance to sintering and in turn to the inhibition of carbon nanotubes formation during the reaction.

γ-Al 2 O 3 sacrificial template method for preparing flower-like Ni–Mg–Al catalysts for dry reforming of methane

Highly dispersed Ni/Al2O3 catalysts for dry reforming of methane prepared by alkaline-induced adsorption process

Highly Dispersed Ni Nanoparticles Supported by Porous Al2O3 Rods for Catalytic Dry Reforming of Methane

Improved performance of Ni/Al2O3 catalyst deriving from the hydrotalcite precursor synthesized on Al2O3 support for dry reforming of methane

Highly dispersed Ni/MgO-mSiO2 catalysts with excellent activity and stability for dry reforming of methane

Porous Nickel‐Alumina Derived from Metal‐Organic Framework (MIL‐53): A New Approach to Achieve Active and Stable Catalysts in Methane Dry Reforming

Engineering of Surface Properties of Ni-CeZrAl Catalysts for Dry Reforming of Methane

Unbounding the Future: Designing NiAl‐based Catalysts for Dry Reforming of Methane

Dry reforming of methane on Ni/mesoporous-Al2O3 catalysts: Effect of calcination temperature

Highly Stable Ni−B/Honeycomb−Structural Al2O3 Catalysts for Dry Reforming of Methane

Modulating Proportion of Ni0 Species Stabilized by Ni2+ on Ni-MgO Catalyst with Superior Stability for Dry Reforming of Methane

5Ni/MgO and 5Ni/MgO + MOx (M = Zr, Ti, Al) Catalyst for Hydrogen Production via Dry Reforming of Methane: Promotor-Free, Cost-Effective, and Handy Catalyst System

Enhancing Coke Resistance of Mg1–xNixAl2O4 Catalysts for Dry Reforming of Methane Via a Doping‐Segregation Strategy

Hierarchical hollow Ni/γ-Al2O3 catalyst derived from flower-like Ni-Al layered double hydroxide with stable catalytic performance for CO2 methanation

Dry reforming of methane over nickel catalysts supported on magnesium aluminate spinels

Ordered mesoporous Ni–Mg–Al2O3 as an effective catalyst for CO2 reforming of CH4

Spherical Ni Nanoparticles Supported by Nanosheet-Assembled Al 2 O 3 for Dry Reforming of CH 4 : Elucidating the Induction Period and Its Excellent Resistance to Coking

Dry Reforming of Methane over Mn-modified Ni-based Catalysts

Dry reforming of methane over Mn-Ni/attapulgite: Effect of Mn content on the active site distribution and catalytic performance

The performances of Ni–MgO@γ-Al2O3 for steam methane reforming prepared by freeze-drying technology

Highly dispersed Fe-decorated Ni nanoparticles prepared by atomic layer deposition for dry reforming of methane