Abstract:Macrosegregation, or compositional heterogeneity, is a very common and serious defect in large steel ingots, which is hard to remove in the following processing procedures. It not only decides the final properties of the product, but also restricts downstream hot working processing severely. This compositional heterogeneity occurs due to the relative motion between the liquid and solid phases during solidification. Therefore, it is necessary to develop an effective method to manufacture large ingots with less macrosegregation. In this work, a novel casting method was proposed to alleviate macrosegregation of large ingots, i.e., layer casting (LC). With this method, alloy melt will be poured into the mould step by step, so that the melt could be solidified layer by layer and the macrosegregation will be alleviated. Both experimental and numerical studies were carried out to verify the feasibility and effectiveness of LC method. Two small Al-4.0% Cu (mass fraction) ingots were cast using two casting methods, conventional casting method, in which melt was cast into mould in one stage, and LC method, in which melt was cast into mould in several stages. Each ingot was sectioned into two parts along the center line, and then the specimens were measured by optical emission spectrometry to obtain the compositional distribution of Cu. Both severe bottom negative segregation and top positive segregation zones were observed in the ingot fabricated by conventional casting method. More homogeneity of compositional distribution was observed in the ingot fabricated by LC method, and the max negative and positive macrosegregation along the center line decreased by 24.6% and 77.2%, respectively. At the same time, a mixed three-phase (equiaxed, columnar and liquid) solidification model was employed to study the solidification processing in large ingots. The macrosegregation formation processes of 100 t and 13 t steel ingots fabricated by both conventional casting and LC methods were numerically simulated. The simulation results indicated that LC method had the capability of alleviating macrosegregation of large steel ingots significantly, compared with conventional casting method. With the increment of ingot size and amount of ladles, LC method had more significant effect on the alleviation of macrosegregation in large ingots. The mechanism of macrosegregation alleviation of LC method was analyzed.

Study on the control of macro/semi-macro segregation in unevenly solidified slabs through optimizing soft reduction process

Analysis of macrosegregation during slab continuous casting using 3D-longitudinal 2D hybrid model

Modeling and Control of Dynamic Soft Reduction in Continuous Slab Casting

Numerical simulation on the centre macrosegregation during Billet continuous casting with the soft reduction

On the Macrosegregation of Continuous Casting of High Carbon Steel Billet with Strand Reduction Process

Modeling the Formation and the Reduction of Macrosegregation in Continuously Cast Steel Slabs

SIMULATION STUDY ON SOFT REDUCTION ZONE FOR CONTINUOUSLY CAST PIPELINE STEEL

Research Progress in Central Segregation Control in Continuous Casting

Numerical Simulation of Macrosegregation in Continuously Cast Slab with Application of S-EMS and MR

Effect of soft reduction process on segregation of a 400 mm thick high-alloy steel slab

Control of macrosegregation at the steel gradient transition by submerged entry nozzle and mold electromagnetic stirring

Analysis of solute redistribution and centerline segregation in continuously cast thin slab

Emulation of Dynamic Secondary Cooling and Soft Reduction in Continuous Slab Casting

Modelling of Solidification Structure and Macro-Segregation in an Industrial DC Cast Slab

Application Situation of Soft Reduction During Process of Slab Continuous Casting

An Experimental Investigation of Continuous Casting Process: Effect of Pouring Temperatures on the Macrosegregation and Macrostructure in Steel Slab

Experimental and Numerical Simulation Study on Layer Casting Method for Composition Homogeneity on Ingot Casting

Study on microsegregation model and MnS precipitation behavior of continuous casting ultra-low sulfur steel slab

Understanding of macro-segregation in direct-chill cast 2024 alloy with intensive melt shearing based on the evolution of microstructure and temperature field

Numerical simulation of macrosegregation during the solidification of steel casting

Application of heat absorption method to reduce macrosegregation during solidification of bearing steel ingot