Abstract:In this work, the ternary Bi2O2CO3/Fe2O3/BiOCl (BOC/Fe2O3/BiOCl) and binary Fe2O3/BiOCl heterojunctions are synthesized by an in-situ hydrothermal method. It is found that the addition amount of FeCl3 has a great influence on the formation of multiple heterojunctions. The XRD and HRTEM results illustrate that the formation of multiple heterojunctions. At FeCl3: BOC = 0.1–0.8:1 (molar ratio), the BOC/Fe2O3/BiOCl ternary heterojunction has formed (S1 0.1Fe-BOC-S5 0.8Fe-BOC). At FeCl3: BOC = 1: 1 and 2.5: 1 (molar ratio), the Fe2O3/BiOCl binary heterojunction has formed (S6 1Fe-BOC, S7 2.5Fe-BOC). Besides, under ultraviolet light irradiation (λ < 400 nm), the photocurrents of S4 0.7Fe-BOC, S5 0.8Fe-BOC, S6 1Fe-BOC and S7 2.5Fe-BOC are 4, 3, 6 and 5 times higher than that of BOC, respectively suggesting the greatly improved charge transfer and separation efficiency. Under ultraviolet light irradiation (λ < 400 nm) within 20 min, ∼40% of rhodamine B (RhB) are photodegraded by S4 0.7Fe-BOC and S5 0.8Fe-BOC, ∼65% of RhB are photodegraded by S6 1Fe-BOC and S7 2.5Fe-BOC. While 8% and 2% of RhB are photodegraded by S1 0.1Fe-BOC and BOC within 20 min, respectively. The apparent reaction kinetic rate constant (ka ) for S1 0.1Fe-BOC (0.024 min−1), S4 0.7Fe-BOC (0.082 min−1), S5 0.8Fe-BOC (0.086 min−1), S6 1Fe-BOC (0.127 min−1) and S7 2.5Fe-BOC (0.093 min−1) are 2.7, 9.1, 9.6, 14.1 and 10.3 times as high as that of BOC (0.009 min−1), respectively. The higher photocatalytic activity of the composite is mainly due to the heterojunction formation, which efficiently improves charge separation and favors the generation of superoxide radical ( O2 –) and hydroxyl radical ( OH). This work provides a simple in-situ hydrothermal method to fabricate multiple heterojunctions with the obviously boosted photoactivity.

One-step conversion of FeOCl/Fe2O3 to BiOCl/Fe2O3 for boosted visible-light-driven photocatalysis

Facile Construction of Nickel-Doped Hierarchical BiOCl Architectures for Enhanced Visible-Light-driven Photocatalytic Activities

In Situ Construction of S-scheme Heterojunctions Between BiOCl and Bi-MOF for Enhanced Photocatalytic CO2 Reduction and Pollutant Degradation

Fabricating BiOCl Nanoflake/FeOCl Nanospindle Heterostructures for Efficient Visible-Light Photocatalysis

Fe3O4 nanoparticle anchored BiOCl platelet as a highly efficient and reusable visible light photocatalyst

In-situ conversion of Bi2O2CO3 to Bi2O2CO3/Fe2O3/BiOCl, Fe2O3/BiOCl heterojunctions and boosted photodegradation activity

Ni2+-assisted catalytic one-step synthesis of Bi/BiOCl/Bi2O2CO3 heterojunction with enhanced photocatalytic activity under visible light

Facile Formation of Bi2O2CO3/Bi2MoO6 Nanosheets for Visible Light-Driven Photocatalysis

Synthesis of BiOCl/TiO2 Heterostructure Composites and Their Enhanced Photocatalytic Activity

One Pot Hydrolysis Synthesis of Fe-Biocl Nanoflower Photocatalysts with Efficient Visible Light Sterilization Performance

One-step solution combustion synthesis of Bi/BiOCl nanosheets: Reaction mechanism and photocatalytic RhB degradation

Uniform Fe2O3 Nanocubes on BiOCl Nanosheets and Its Improved Photocatalytic Activity

Enhancement of visible photocatalytic performances of a Bi2MoO6-BiOCl nanocomposite with plate-on-plate heterojunction structure.

BiFeO3/Bi2Fe4O9 S-scheme Heterojunction Hollow Nanospheres for High-Efficiency Photocatalytic O-Chlorophenol Degradation

Tunable BiOCl hierarchical nanostructures for high-efficient photocatalysis under visible light irradiation

Facile in situ synthesis of a Bi/BiOCl nanocomposite with high photocatalytic activity

One-step route to α-Bi2O3/BiOX (X = Cl, Br) heterojunctions with Bi2O3 ultrafine nanotubes closely adhered to BiOX nanosheets

Enriched surface oxygen vacancies of BiOCl boosting efficient charge separation, whole visible-light absorption, and photo to thermal conversion

In Situ Synthesis of Uniform Fe2O3/BiOCl P/n Heterojunctions and Improved Photodegradation Properties for Mixture Dyes.

Oxygen vacancies induced narrow band gap of BiOCl for efficient visible-light catalytic performance from double radicals

Photoelectrochemical and photo-Fenton mechanism of enhanced visible light-driven nanocatalyst synthesis of ZnFe2O4/BiOI