Effortless Fabrication of Bi2O3‐Co3O4 Nanocomposite Catalyst: Harnessing Photocatalytic Power for Efficient Cationic Dye Degradation
Debapriya Pradhan,Nibedita Nayak,Monalisha Kanar,Suresh Kumar Dash
DOI: https://doi.org/10.1002/slct.202400217
2024-04-03
ChemistrySelect
Abstract:A new photocatalyst called Co3O4‐Bi2O3 was created utilizing a simple affordable co‐precipitation process with cobalt nitrate and bismuth nitrate as metal precursors. The structural and optical characteristics of the produced material were characterized using XRD, FTIR, TEM, SEM‐EDS, XPS, UV‐DRS, PL, BET, and TGA.The band gap energy of virgin Co3O4 and Bi2O3 was found to be 2.4 and 2.7 eV, respectively, whereas that of the heterojunction composite was lowered to 2.1 eV.The modified cobalt oxide composites perform better as photocatalysts than the pure ones due to their narrow band gap energy, increased surface area, excellent absorption in the visible range, and decreased charge carrier recombination.The photocatalytic activity of the composite was assessed by altering factors such as pH, dye concentration, catalyst dosage, temperature, and duration. Within 60 minutes, the heterojunction composite degraded MB and MG to 98 % (at pH=11) and 97 % (at pH=9), respectively.The photodegradation of both dyes follows a pseudo‐first order kinetic model, and the thermodynamic investigation revealed that the process is spontaneous and endothermic.To investigate the function of radicals in degradation mechanisms, a reactive species trapping analysis was performed, and the important participation of the hydroxyl radical was discovered.The modified catalyst demonstrated a modest decrease in degrading efficiency after the fifth cycle, making it suitable for practical application. In the photodegradation method, electrons in the Valence band of cobalt oxide and bismuth oxide were stimulated and hopped to the conduction band when exposed to sun radiation. The electrons from the CB of Bi2O3 transferred to the CB of Co3O4 resulting reduction in the charge carrier recombination. A cost‐effective and simple co‐precipitation approach was used to create an efficient photocatalyst Co3O4‐Bi2O3 with identical stoichiometry (1 : 1 of both Co3O4 and Bi2O3). XRD, FTIR, TEM, SEM‐EDS, XPS, UV‐DRS, PL, BET, and TGA were used to characterize the produced material's structural and optical properties. The presence of a single phase spinel structure with a distinctive plane (311) was verified by the XRD peak of 2 at 36.9° for Co3O4‐Bi2O3. The SEM pictures revealed clustered consolidated spheres, suggesting particle homogeneity and high interconnectedness. The HR‐TEM and SAED pictures revealed an average crystallite size of 28 nm for the Co3O4‐Bi2O3 heterojunction. The UV‐DRS spectral data demonstrated a 2.1 eV reduction in band gap energy for Co3O4‐Bi2O3 (whereas Co3O4 is 2.4 eV and Bi2O3 is 2.7 eV). Under solar light irradiation, pristine Co3O4, Bi2O3, and Co3O4‐Bi2O3 composites were investigated for photocatalytic degradation of Methylene Blue (MB) and Malachite green (MG) dyes. By adjusting factors such as pH, starting dye concentration, catalyst dosage, and agitation duration, the optimal efficiency was determined. The acquired results showed Co3O4‐Bi2O3 ′s superior activity over both precursors. The composite obtained maximal degradation of 98 % (at pH=11) and 97 % (at pH=9) for MB and MG, respectively. The enhanced photo degradation activity of Co3O4‐Bi2O3 can be due to larger visible light absorption, increased surface area, and decreased h+/e− recombination. The reactive species trapping study was performed to determine the importance of superoxide and hydroxyl radicals during photo degradation. Dye degradation was governed by a pseudo‐first‐order kinetic model. The reusability and stability of Co3O4‐Bi2O3 were confirmed by utilizing the same material for five consecutive runs with both MB and MG dyes. Mass spectra analysis provided insights into the successful degradation of dyes, elucidating intermediate products. The synthesized Co3O4‐Bi2O3 nanocomposite offers unrivalled advantages in terms of structural and optical properties, superior photocatalytic activity, and remarkable stability, making it a promising candidate for efficient dye degradation applications without the formation of toxic by‐products.
chemistry, multidisciplinary