Nanoscale Lanthanum Carbonate Hybridized with Polyacrylic Resin for Enhanced Phosphate Removal from Secondary Effluent
Yue Sun,Xinlei Feng,Weisheng Zheng
DOI: https://doi.org/10.1021/acs.jced.0c00352
2020-08-21
Abstract:The removal of phosphate from water has attracted increasing attention because of the dominant role of phosphate in eutrophication. In this study, a novel nanoscale hybridized adsorbent, , was fabricated by immobilizing nanosized lanthanum carbonate (NLC) into the pores of the macro-porous polyacrylic anion exchanger D213 through an in-situ precipitation method for phosphate adsorption from wastewater. exhibited excellent pH tolerance and possessed a high selectivity for phosphate in the presence of competing anions (Cl<sup>–</sup>, NO<sub>3</sub><sup>–</sup>, SO<sub>4</sub><sup>2–</sup>, SiO<sub>3</sub><sup>2–</sup>, and HCO<sub>3</sub><sup>2–</sup>) and organic acids (humic, tannic, and gallic acids). The maximum phosphate adsorption capacity reached 53.64 mg P/g at 30 °C. Moreover, fixed-bed column adsorption experiments demonstrated that could effectively treat 2400 bed volumes of real secondary effluent (phosphate concentration decreased from 2.0 to <0.5 mg P/L). The exhausted could be regenerated easily using a binary solution of NaCl (1.5 mol/L)–Na<sub>2</sub>CO<sub>3</sub> (3 mol/L), and no significant capacity loss was observed during the recycling for column adsorption–desorption. The underlying mechanism of phosphate adsorption was investigated by a combination of Fourier-transform infrared, transmission electron microscopy, and X-ray photoelectron spectroscopy, and the formation of LaPO<sub>4</sub>·<i>x</i>H<sub>2</sub>O was suggested to be the main pathway in the separation process of phosphate from real secondary effluent.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.jced.0c00352?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.jced.0c00352</a>.Effect of lanthanum chloride concentration on phosphate adsorption; chemical structure of D213 and D201; SEM images of D213 and ; XPS analysis of ; FTIR spectra of D213, , and after P adsorption; phosphate species distribution versus pH; adsorption isotherm of phosphate by ; La dissolution from ; XRD diffractograms; TEM image of after P saturation; Langmuir and Freundlich model isotherm parameters of phosphate adsorption onto ; comparison of phosphate adsorption capacity for different La-based materials; and thermodynamic parameters of sorption for phosphate (<a class="ext-link" href="/doi/suppl/10.1021/acs.jced.0c00352/suppl_file/je0c00352_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
engineering, chemical,thermodynamics,chemistry, multidisciplinary